Abstract
Objective The aim of this study was to evaluate the effect of reducing the bone to cast distance
on the resistance of the pin to cyclic loading in equine transfixation pin casts.
Study Design Eleven pairs of cadaveric equine third metacarpal bones were prepared and one 6.3/8.0 mm
transfixation pin was placed in standard fashion 10 mm proximal to the distal physeal
scar into each bone. One metacarpus of each pair was tested with a distance of 10 mm
(10 mm group) and the contralateral metacarpus with a distance of 20 mm (20 mm group)
between the outer cortex of the bone and the fixation of the pin. Eight pairs were
tested using a simplified test set-up in which the pins were fastened at both ends
to polyoxymethylene-copolymer sleeves. The pins of the remaining three pairs of bones
were incorporated into a fibreglass cast. All specimens were tested under cyclic loading
until failure of the pin in axial compression.
Results All pins failed uni- or bilaterally at clinically relevant load levels. Pins of the
10 mm group endured significantly (p < 0.05) higher load levels and total number of cycles until failure compared with
the pins of the 20 mm group.
Conclusion The distance between the bone surface and the cast at the location of pin insertion
has a significant effect on resistance of the pins to cyclic loading. Therefore, the
amount of padding applied underneath an equine transfixation pin cast can have an
influence on the overall stability and durability of the construct.
Keywords
horses - transfixation pin cast - pin breakage - cyclic loading - padding