Introduction
Water molecules existing at the interface between biomaterials and biological fluids
play a crucial role in determining the fate of the components present in the fluids
before and after adsorption on the surface of the material. Interactions between fluid
components and surfaces occur hierarchically in the order of water, proteins, and
cells.[1] We previously studied the hydration state of biomaterials and observed that biocompatible
synthetic polymers form three types of water: non-freezing water (NFW), intermediate
water (IW), and free water (FW).[2] It is well known that biomacromolecules such as protein, DNA, and RNA also contain
IW. In contrast, non-biocompatible synthetic polymers do not enable IW formation.
IW plays a key role in the biocompatibility of polymers and can influence protein
adsorption and cell adhesion.[2f] Thus, molecular design that allows for the formation of IW offers significant advantages
to those interested in synthetic biomaterials.
Water-insoluble polymers typically exhibit poor biocompatibility, as their hydrophobic
characteristics often induce protein adsorption and denaturation. However, poly(2-methoxyethyl
acrylate) (PMEA)[2e] is an exception to this general rule. PMEA is a biocompatible synthetic polymer
with superior surface antithrombogenicity, despite the fact that it is insoluble in
water. The biocompatibility of PMEA is attributed to the methoxyethyl side chain,
which ensures a balance between hydrophilicity and hydrophobicity, leading to the
formation of IW.[2f] Owing to the attractive features of IW combined with water insolubility, PMEA has
been used as an antithrombotic treatment material in biomedical devices.[3] We have previously investigated various polymeric materials inspired by the chemical
structure of PMEA to elucidate a suitable structure for controlling the formation
and content of IW.[4] However, the structure still needs to be optimized. For this purpose, we have focused
on cyclic structures in this study. The biological response of a cyclic polymer is
dissimilar to that of a linear polymer. This difference is rooted in the disparities
between the polymer chain mobilities due to the loss of the chain end.[5] As mentioned earlier, the hydration states, especially IW, directly affect the biological
response of biomaterials. However, to date, there have been no reports on the relationship
between the chain-end effect and IW formation. In this study, we synthesized a cyclic
PMEA and described the chain-end effect on IW formation by comparative studies with
a linear PMEA. The hydration-state analyses were performed by differential scanning
calorimetry (DSC) and atomic force microscopy (AFM).
Results and Discussion
We synthesized the linear PMEA (5) and cyclic PMEA (7) according to the pathway outlined in [Scheme 1]. Initially, the symmetrical bromopropanoate derivative 1 was synthesized by the condensation reaction of ethylene glycol and 2-bromopropanoyl
bromide.[6] The sodium salt of ethyl trithiocarbonate 2 was prepared by the addition of sodium ethanethiolate and carbon disulfide.[7] The mono-bifunctional chain transfer agent, 3, was obtained via the SN2 reaction between 1 and 2.[8] The obtained compounds 1–3 were characterized using 1H and 13C NMR spectroscopies ([Figures S1–S3]). We conducted the reversible addition–fragmentation chain transfer (RAFT) polymerization
of 2-methoxyethyl acrylate (MEA) with 3 and isolated the polymer, a yellow-colored viscous liquid, by reprecipitation.[9] The chemical structure of the product was determined by 1H NMR spectroscopy. The number-average molecular weight (M
n,NMR, M
n,SEC) and polydispersity index (Ð) were evaluated by 1H NMR and size-exclusion chromatography (SEC) analyses, respectively. The SEC chromatograph
was symmetrically unimodal and shifted toward a high molecular weight as the polymerization
process proceeded ([Figure 1], gray and black lines). The experimental value of M
n,SEC agreed with the calculated theoretical value based on the monomer conversion (M
n,SEC = 76,300 g mol−1, M
n,theor = 75,100 g mol−1), and the dispersity was remarkably narrow (Ð = 1.06). The presence of MEA units adjacent to the trithiocarbonate moieties was
confirmed by the characteristic 1H signal at ca. 4.7 ppm ([Figure S4], black line). By end-group analysis based on this signal, the M
n,NMR was estimated to be 78,200 g mol−1, which also corresponded with the M
n,theor and M
n,SEC values. From these results, we concluded that the RAFT polymerization of MEA proceeded
successfully to give well-defined acyclic telechelic PMEA, 4. An end group, especially a hydrophobic and bulky group, often significantly affects
the physical properties and morphology of polymers.[10] Consequently, 4 is not suitable as a standard linear PMEA for evaluating the hydration state. Thus,
desulfurization of 4 was performed by radical-induced reduction,[11] and the resultant polymer was purified by reprecipitation to give the pure desulfurized-polymer
5, as a colorless viscous liquid.[12] The SEC trace of 5 shifted slightly toward a low molecular weight while maintaining a narrow shape (M
n,SEC = 75,900 g mol−1, Ð = 1.09) ([Figure 1], red line). In addition, the 1H NMR peak corresponding to the methine moiety in the MEA units adjoining the trithiocarbonate
groups was found to disappear ([Figure S4], red line). This observation implies the successful progression of the reduction
and translation of the end groups into hydrocarbons. The following experiments used
5 as the linear PMEA. Next, we attempted to prepare 7 via intramolecular cyclization of 6.[13] In general, RAFT-synthesized polymers contain a thiocarbonylthio moiety at the end
of the polymer chain that can be translated to a thiol group by treatment with nucleophiles
and ionic reducing agents[11b] such as amines,[14a] hydroxide,[14b] and borohydride.[14c]
Scheme 1 Synthetic route to the linear and cyclic PMEA. (i) 2-Bromo-2-methylpropanoyl bromide,
pyridine, in THF, RT, 12 h. (ii) 1) sodium hydride, in diethyl ether, 0 °C, 30 min;
2) carbon disulfide, in diethyl ether, RT, 2 h. (iii) In acetonitrile, RT, 24 h. (iv)
MEA, AIBN, in toluene, 70 °C, 1 h. (v) TTMSS, V-70, in toluene, 40 °C, 12 h. (vi)
isobutylamine, in THF, RT, 2 h. (vii) iron(III) chloride, in diethyl ether/THF (v/v) = 3/1,
RT, 1 month.
Figure 1 SEC chromatograms of acyclic telechelic PMEA before (4, black) and after (5, red) desulfurization and 3 (gray).
In the presence of an oxidant, the thiol group spontaneously forms a disulfide bond,
and this reaction is often employed to prepare cyclic structures.[15] End-group conversion of 4 was carried out by treating with isobutylamine to give the desired thiol-terminated
PMEA 6, as a colorless viscous liquid. Subsequently, 6 was dissolved in a large amount of diethyl ether/THF (v/v = 3/1) solution and treated
with the strong oxidizing agent iron(III) chloride under high-dilution conditions
to allow formation of a disulfide bond.[15a] SEC analyses were then performed on 6 at various time intervals using the same polymer concentrations ([Figure 2]). With an increase in the reaction time, the peak of the initial linear polymer
between 18.5 and 20.7 min decreased, and a new peak appeared in a region of lower
molecular weight (19.8–21.3 min). This result suggests that the intramolecular cyclization
reaction proceeds via disulfide formation because the SEC trace typically shifts to
a higher molecular weight when intermolecular disulfide bonds are formed. Most importantly,
the peak-top molecular weights of the starting material (M
p,L) and the newly generated component (M
p,C) were 88,200 g mol−1 and 63,500 g mol−1, respectively. The ratio of these molecular weights (M
p,C/M
p,L), which is an index that indicates the generation of cyclic polymers, was calculated
to be 0.72. The value is consistent with those in previous reports.[16] The resultant polymer was isolated, and a part of it was reduced using a zinc/acetic
acid system and analyzed by SEC measurement ([Figure S5]). The peak of 7 clearly shifted toward a higher molecular weight and almost matched that of the initial
linear polymer, suggesting that the resultant polymer has a cyclic structure. The
chemical structure of the resultant polymer was determined by 1H NMR spectroscopy and assigned to the PMEA backbone ([Figure S6]). In addition, the glass transition temperature (T
g) of the polymer after oxidization was estimated to be −36.5 °C from the DSC thermogram,
which differed appreciably from the transition temperature of 5 (−38.8 °C) ([Figure S7]). It is well known that cyclic polymers show higher T
g values than linear polymers.[17] Thus, we concluded that the obtained polymer, 7, consists mostly of a cyclic structure (>80%) and can be used to evaluate the impact
of the chain-end effect on hydration states. 7 was used in subsequent experiments as the cyclic PMEA.
Figure 2 SEC chromatogram changes of thiol terminated-telechelic PMEA, 6, with along through progress of oxidization using iron(III) chloride.
The precise amounts of hydration water (NFW, IW, and FW) in the hydrated polymers
were easily determined by DSC measurements.[2f] Polymers 5 and 7 were saturated in pure water and evaluated based on DSC measurements ([Figure S8]). For both polymers, the cold crystallization temperature of the water, derived
from IW, was confirmed to be approximately −40 °C. The T
g,dry of 7, without the chain end, was higher than that of 5 owing to the decreased mobility of the polymer chain. In contrast, the T
g,water of 7 (−50.8 °C) was lower than that of 5 (−48.4 °C). In general, T
g decreases when the water content is high, even for the same polymer species.[18] These results suggest that the amount of diffused water in 7 is larger than that in 5. The content and quantity of the three types of water per unit weight of the polymer
were calculated from the enthalpy variation of water and the weight difference between
the dry and wet polymers ([Figure 3a]). The water contents of hydrated 5 and 7 were estimated to be 9.4% and 12.2%, respectively. Thus, polymer 7, without the chain end, took up more water because the free volume of the cyclic
polymer was smaller than that of the linear polymer. In fact, it has been reported
that cyclic polymers can contain significantly more water than linear polymers as
they experience less entanglement.[19] Importantly, the increased water content in 7 is mostly composed of FW and IW (76%). It is known that water confined in a nano
space exhibits freezing behavior similar to FW and IW depending on the space size.[20] The diameter of the nano space in the cyclic polymer 7 in pure water 
is estimated to be about 2.1 nm from the following equation[21]:
where n is the number of segments (polymerization degree), and b is the length of each segment. The obtained value is optimum for water to form clusters,
that is, cold crystallization.[20a] We concluded that a molecular structure without a chain end like that in 7 can provide an appropriate-sized nano space to promote the diffusion of water molecules
and the formation of FW and IW. Thus, we clarified that the chain end of the polymer
affected the hydration state; thus, the formation of IW in pure water was nourished
by cyclization. Subsequently, the hydration states of the polymers were examined in
phosphate-buffered saline (PBS) using DSC measurements ([Figure S9]). These experiments are essential to identify hydrated water that is crucial for
biocompatibility because biological responses usually occur under physiological ionic
conditions. [Figure 3b] shows the quantified hydrated water in the polymers. Although the T
g,PBS values of these polymers were almost the same, the water content of hydrated 7 (6.9%) was lower than that of 5 (8.2%). In addition, the amounts of FW and IW in 7 were slightly lower than those in polymer 5.
Figure 3 Summary of hydration state analyses for 5 and 7 in pure water (a) and PBS (b) systems.
These results indicated that the formation of FW and IW due to confinement in the
nano space of 7 was partially expelled by the osmotic effect and shrinkage of the polymer matrix,[4d] suggesting that the chain length of 7 was too long to maintain the IW. This is because the nano spaces formed in a large cyclic polymer, wherein the main
chain is relatively flexible compared to that of a small cyclic polymer, easily collapse.
This osmotic pressure induced the shrinkage of 7 compared with 5 because the cyclic polymer has low mobility and easily interacts between the MEA
units in a molecule. Therefore, water molecules are interrupted to approach the MEA
units, resulting that the NFW content formed on 7 in PBS was drastically declined compared with 5. Thus, it would be possible to control IW formation by adjusting the length of the
polymer chains and optimizing the size of the nano space.
Interactions between polymers and biomolecules occur at the interfaces. Therefore,
it is important to understand not only the fundamental physical properties of the
polymer and the hydrated state obtained by DSC, but also the hydration state of the
polymer surface. We prepared surfaces of 5 and 7 by spin-coating and measured water and air contact angles to investigate the hydration
state. The water contact angles immediately after the aqueous contact were estimated
to be 82.4° ± 0.5° and 90.1° ± 0.5°, respectively. After 30 s, the water contact angle
of 5 decreased to 40.0° ± 0.1° via the polymer chain orientation. In contrast, the water
contact angle of 7 did not change significantly (83.5° ± 0.2°) ([Figure S10]). These observations reflect that the chain orientation in polymer 7 occurred slowly because the mobility of 7 was lower than that of 5. The air contact angle was measured after immersion in PBS. The air contact angles
of 5 and 7 are almost the same (147.8° ± 0.9° and 147.3° ± 1.4°, respectively), indicating that
the water contents of 5 and 7 are almost the same at the polymer/PBS interface. The hydration state at the interface
was analyzed using AFM in greater detail. AFM is an efficient method for deciphering
the hydration state at the polymer/water interface. Recently, we reported that the
structure at the polymer/water interface differs depending on the presence of IW.[22a] It was previously reported that a linear PMEA exhibited a heterogeneous interfacial
structure at the polymer/PBS interface based on the phase separation of polymer-rich
and water-rich domains.[22b] Furthermore, protein adsorption was suppressed in water-rich domains where a large
amount of IW existed.[22c] In this study, a similar structure was also observed at the 7/PBS interface ([Figure 4]). The bright area is polymer-rich domains and the dark area is water-rich domains.
Because tiny polymer density in the water-rich domains is not detectable by AFM, polymer-rich
domains are observed as nanometer-scale protrusions at the interface. [Figure 4] suggests that the surface of 7 was filled with IW. We perceive that the polymer-rich domains (island parts) are
larger and the area covered by water-rich domains is smaller for 7 than for 5. The estimated area percentages of the water-rich domains that have been averaged
from the image analysis of five 5 μm × 5 μm images were 84.8 ± 0.7% for 5 and 79.5 ± 1.0% for 7. The reason for the formation of larger polymer-rich domains in 7 compared to 5 is that the cyclic chains facilitated phase separation at the polymer/water interface.
It is expected that the water-rich domain includes a larger amount of IW than the
polymer-rich domain in previous studies.[22b]
[d] Thus, we concluded that 7 retains a smaller amount of IW than 5 at the interface as well as in the bulk state, as depicted by the DSC measurements
([Figure 3b]). The difference between 5 and 7 is more significant than that in [Figure 3b] because the water content of PMEA in the interface is much higher than that in the
bulk state.[23] Platelets sufficiently suppressed the adhesion and activation on the surfaces of
both polymers as compared to the bare polyethylene terephthalate surfaces ([Figure S11]). Previously, we had reported that the platelet adhesion on the PMEA brush samples
was quite low when the area percentage of the water-rich domain was over 40%.[22d] These results indicated that a sufficient amount of IW was present at both interfaces
to prevent platelet adhesion.
Figure 4 AFM images of (a) 5 and (b) 7 in PBS.
Conclusions
In this study, we synthesized well-defined linear and cyclic PMEAs and investigated
the chain-end effect for IW formation using comparative experiments. DSC analysis
indicated that the amount of IW in the linear and cyclic PMEAs showed a minor difference
in the PBS system. In contrast, the cyclic structure provided nano spaces of moderate
size and promoted the formation of IW in the pure water system. AFM observations indicated
that the surface of the cyclic PMEA exhibited slightly different phase separation
behavior from that of the linear PMEA. Hence, the chain-end effect certainly influenced
the hydration state, including the IW. The insights obtained from this study suggest
the possibility of controlling IW formation, and provide a promising opportunity for
the design of biomaterials based on “the intermediate water concept”.