Rhodanine-Bridged Core-Expanded Naphthalene Diimide Derivatives for n-Type Semiconductors
Publication History
Received: 28 February 2020
Accepted after revision: 06 April 2020
Publication Date:
27 May 2020 (online)
Abstract
The core expansion of naphthalene diimides (NDIs) is an effective strategy to modulate frontier molecular orbital energy levels and improve device performances. Herein two new rhodanine-bridged and core-extended NDIs T1 and T2 were designed and synthesized. The rhodanine moiety could act not only as a π-spacer to enlarge the molecular conjugated system, but also as an electron-donating unit to tune the molecular energy levels. As a result, both T1 and T2 showed slightly lower lying LUMO energy levels (< − 4.2 eV) by ca. 0.1 eV and narrower optical band gaps (ca. 1.5 eV) by 0.5 eV compared to those of n-type organic semiconductor (OSC) NDI2DT-DTYM2.The solution-processed organic thin-film transistors based on T1 and T2 exhibited electron motilities in the range of 10−4–10−3 cm2 V−1 s−1, and the inverted perovskite solar cells constructed using T2 as electron transport materials provided a power conversion efficiency value of 8.82%. The results demonstrated that embedding rhodanine units in a NDI2DT-DTYM2 backbone is an effective approach to tune the energy levels and optical properties of OSCs, providing a new way to construct novel n-type OSCs with multifunctional optoelectronic applications.
#
Key words
rhodanine - naphthalene diimides - organic semiconductors - organic thin-film transistors - electron transport materialsIntroduction
As the key active-layer components of organic optoelectronic devices, organic semiconductor (OSC) materials have attracted considerable attention owing to their various advantages such as mechanical flexibility, low cost, solution-processability, and tunable frontier molecular orbital energy levels by rational molecular design.[1] [2] [3] [4] [5] [6] [7] Suitable HOMO and LUMO energy levels are a vital prerequisite for achieving high-performance OSCs.[8] For instance, the high-lying HOMO and low-lying LUMO energy levels should be close to the work function of the electrode, which are beneficial for hole and electron injection, respectively, and in turn to achieve high charge carrier mobility in organic thin-film transistor (OTFT) devices.[9] In addition, a good alignment of the LUMO energy levels with the conducting band minimum of the perovskite materials is also important for the dynamics of charge transfer and extraction behavior at the perovskite–electron transport material (ETM) interface, which play an important role in determining the performance parameters such as open-circuit voltage (V oc), short-circuit density (J sc) as well as the power conversion efficiency (PCE).[10] The construction of π-expanded conjugated semiconductors with the push–pull strategy is one of the most successful approaches to modulate the HOMO and LUMO energy levels of OSCs.[11] In this manner, more and more extended π-conjugated OSCs with high performance burgeoned during the past decades.[12] [13]
1,4,5,8-Naphthalene diimides (NDIs),[12] [14] [15] among the most versatile and fascinating class of building blocks, have been the subject of great research interest due to their intrinsic properties such as high electron affinity, good charge carrier mobility, and remarkable thermal and oxidative stability. As a result, the past decades have witnessed extensive developments of NDIs[14] [15] as organic conjugated frameworks for the synthesis of multifunctional structures in supramolecular chemistry, chemical sensors, molecular switching devices, biomedical application, and OTFT and photovoltaic devices. At present, the chemical-structure modifications of NDIs are mainly focused on the following three paths: (i) the modulation of N-substituent alkyl chains for influencing solution processability, molecular packing, film microstructure, and in turn to tune charge transport of OTFT devices[16] [17] [18]; (ii) the core modification of NDIs including σ-bond-linked substituents (including electron-withdrawing groups and electron-donating units) for modulating molecular optical/electronic properties[19] [20] [21]; (iii) the lateral core expansion of NDIs by fusing five- and six-membered rings either on one side or both sides of the NDI core to regulate the HOMO and LUMO energy levels as well as the intramolecular and/or intermolecular interactions for efficient charge transport.[22] [23] Among such heterocyclic (carbazole, imidzaole, thiophene rings, etc. ) fused NDIs,[16] [17] [18] [19] [20] [21] [22] [23] NDI-DTYM2 derivatives bearing two (1,3-dithiol-2-ylidene)malononitrile (DTYM) are the most representative building blocks, which exhibit excellent electron mobilities and ambient stability in OTFT devices.[5a] Therefore, the core expansion of NDIs by sulfur-containing heterocycles and end capped with an electron-withdrawing group is a successful strategy to obtain high-performance OSCs. On the other hand, sulfur-heterocycle-fused NDI materials, which effectively function as nonfullerene ETMs in “regular” or “inverted” perovskite solar cells (PSCs), have far less been explored.[15a] Consequently, novel n-type OSCs based on large π-conjugated NDIs for OTFT and PSC applications are still in urgent pursuit.
To further develop core-expanded NDI chemistry, here we report two rhodanine-bridged NDI derivatives T1 and T2 ([Scheme 1]) synthesized via the core-expanded strategy. This molecular design is based on the following considerations: (i) the incorporation of π-conjugated spacer rhodanine not only extends the π-conjugation of NDIs, but also acts as a second “donor” moiety to modulate the optical/electronic properties of the molecules[24]; (ii) the selection of malononitrile as the end-capped electron-withdrawing group, which could effectively deepen the LUMO energy levels of A-π-D-A-D-π-A-type conjugated small molecules, which are crucial for achieving ambient-stable electron injection and conduction in their OTFT devices.[5a] [17a]
#
Results and Discussion
The synthetic routes of T1 and T2 are shown in [Scheme 1], and the synthetic details of the intermediate A3 and T1 and T2 are provided in the Supporting Information ([Scheme S1] [S2] [S3] [S4]).[25] The facile nucleophilic aromatic substitution reaction (SNAr) of A3 could be performed efficiently via a mild one-pot synthetic method with a yield of 51.2% for T1 and 67.2% for T2, respectively.[17a] This one-pot synthesis undergoes an in-situ formation of rhodanine-bridged dithiolate sodium salts (first step) and then an SNAr reaction (second step) in THF at room temperature, allowing an easy and low-cost access to diverse 1,3-disulfur heterocyclic-fused NDI-based n-type semiconductors. A mixture of trans/cis target compounds (T1 and T2) was obtained but the separation of the trans-T1 and cis-T1 (as well as the trans-T2 and cis-T2) failed with column chromatography and high-performance liquid chromatography, which probably ascribed to identical molecular polarity of the trans- and cis- isomers. The chemical structures of A3, T1, and T2 (trans-/cis- isomers) were well characterized by 1H and 13C NMR spectroscopy, high-resolution mass spectroscopy, FT-IR analysis as well as elemental analysis ([Figure S8] [S9] [S10] [S11] [S12] [S13] [S14] [S15] [S16] [S17] [S18] [S19] [S20] [S21] [S22] [S23] [S24]). Both T1 and T2 are readily soluble in common organic solvents such as chloroform, chlorobenzene, and 1,2-dichlorobenzene (>5 mg/mL) at room temperature, allowing the solution-processable fabrication of optoelectronic devices based on them. Thermogravimetric analysis (TGA) measurements revealed that T1 and T2 have excellent thermal stability with decomposition temperatures (T d, 5% weight loss) of 387 °C and 380 °C, respectively ([Figure S1]). Differential scanning calorimetry (DSC) characterization was also carried out under an inert atmosphere, and no apparent thermal transition signal for T1 and T2 was observed in the entire scanning range: 25–350 °C ([Figure S2]). The results indicated that T1 and T2 exhibit good thermal stability and their thin films can be treated over a broad range of annealing temperatures.[26]
The ultraviolet–visible–near infrared (UV-vis-NIR) absorption spectra of T1 and T2 in chlorobenzene solution and in thin films were measured to investigate their optical properties ([Figure 1]); the corresponding data are summarized in [Table 1]. The absorption spectra of NDI2DT-DTYM2 in solution and in thin film were also recorded for comparison ([Figure S3]). As shown in [Figure 1], both in dilute chlorobenzene solution and in thin films, T1 and T2 display a typical dual-band absorption feature covering 300–800 nm. The sharp one at the high-energy region (350–500 nm ) is attributed to π-–π* transitions of the conjugated backbone, and the strong and wide absorption (550–800 nm) can be ascribed to the strong intramolecular charge transfer transition between the donor and acceptor units.[17] [27] The chemically similar structures of T1 and T2 bearing different amide alkyl chains in rhodanine units show nearly identical absorption spectra both in solution and in thin films with nearly identical peak values of their maximum and onset absorptions ([Table 1]), suggesting that their optical properties are insensitive to the structure of the N-alkyl chain in the rhodanine moiety as expected.[12a] The maximum of the 0–0 vibrational peak of thin films shows a large red shift of about 25 nm compared to those of T1 and T2 in solution. Moreover, the absorption intensities of the 0–1 and 0–0 vibrational peaks from solution to thin film changed greatly, indicating the highly changed conformation of T1 and T2, and probably the stronger intermolecular π–π stacking in the solid state originated from the J-type aggregate pattern.[28] It is worth noting that the absorptions of T1 and T2 in thin films extend to the NIR region with the absorption onset at 821 and 832 nm, respectively, and the corresponding E g opt values of 1.51 and 1.49 eV, respectively. In comparison with NDI2DT-DTYM2 (E g opt = 2.0 eV), the dramatic down-shift band gaps of T2 and T2 possibly ascribe to the larger extension of the π-conjugated system of T1 and T2 with the implanted rhodanine unit as a spacer. Thus, implanting rhodanine units into OSC backbones is a potent strategy to impact on their intramolecular and intermolecular interactions and efficiently tunes the optical properties of OSC materials.[24]
Compound |
T d (°C) |
λ max sol. (nm) |
λ max 0–0 sol. (nm) |
λ max 0–1 sol. (nm) |
λ max 0–0 film (nm) |
λ max 0–1 film (nm) |
E g opt (eV)[a] |
E LUMO (eV)[b] |
E HOMO (eV)[c] |
---|---|---|---|---|---|---|---|---|---|
T1 |
387 |
414 |
686 |
627 |
713 |
652 |
1.51 |
–4.20 |
–5.71 |
T2 |
380 |
414 |
688 |
627 |
713 |
654 |
1.49 |
–4.20 |
–5.69 |
a Estimated from the onset absorption of thin films.
b Calculated from the first onset reductive potential. E LUMO = −4.44 − E red1 onset.
c E HOMO = E LUMO − E g opt.
To investigate the electrochemical properties of T1 and T2, cyclic voltammetry (CV) measurements were performed ([Figure 2] and [Table 1]). Compounds T1 and T2 exhibit a nearly identical irreversible reduction process in CHCl3, in which the first onset reductive potential (E red1 onset) is at approximately –0.24 V. The LUMO energy levels, estimated by CV [E LUMO = – (E red1 onset + 4.44) eV],[29] are both at −4.20 eV. Compared to NDI2DT-DTYM2, the LUMO energy levels of T1 and T2 are shifted upward by ca. 0.1 eV, which is likely due to the rhodanine unit that not only as a π-conjugated spacer regulates its optical properties ([Figure 1]), but also as a relatively strong electron-donating moiety effectively tunes its electronic structure ([Figure 2]). The relative low-lying LUMO energy levels of T1 and T2 enable them to be potential n-type OSCs.
To evaluate the semiconducting properties of T1 and T2, OTFT devices were fabricated by spin-coating the solutions of T1 and T2 onto octadecyl trichlorosilane (OTS)-modified Si/SiO2 substrates. Au source/drain electrodes were deposited on the active layer to afford OTFTs with a bottom-gate top-contact device configuration. The OTFT devices were tested in a glovebox with a nitrogen atmosphere, and the OTFT characteristics of the devices, thermal annealed at different temperatures, are collected in [Table 2]. Additionally, the histograms of performance distributions of T1- and T2-based OTFT devices are presented in [Figure S5]. As shown in [Figure 3], all the devices exhibited n-type semiconductor characteristics, which correlate well with the aforementioned CV results ([Figure 2]). The as-spun OTFT devices based on compounds T1 and T2 showed electron mobilities (μ e) in the range of 10−3–10−4 cm2 V−1 s−1, and current on/off ratios (I on/off) in the range of 102–105. When subjected to thermal annealing at 80 °C, the μ e values of OTFTs with thin films of T1 and T2 were improved ([Table 2]). For instance, the as-spun OTFT devices based on T1 showed an average μ e value of 1.44 × 10−3 cm2 V−1 s−1, and a current on/off ratio (I on/off) of 103–105. For OTFT devices based on T1 and annealed at 80 °C, the average μ e was enhanced to 1.76 × 10−3 cm2 V−1 s−1 and its maximum μ e up to 4.11 × 10−3 cm2 V−1 s−1. A slight decrease in mobility of the T1-based OTFT devices was observed after annealing at 120 °C. The performance of OTFTs based on T2 exhibit analogous response to thermal-annealing treatment. After annealing at 80 °C, the optimal μ e of 3.9 × 10−4 cm2 V−1 s−1 was obtained for the T2-based OTFT devices ([Table 2]). It should be mentioned that the T1-based devices show about 1 order of magnitude higher μ e values than those of T2-based ones. The drastically different performance of OTFT devices is probably the result of different film microstructures influenced by the alkyl chain in the rhodanine moiety, which will be discussed below.[30]
Compound |
T a (°C) |
μ e Max (Avg) (cm2 V−1 s−1)[a] |
V T (V)[a] |
I on/I off [a] |
---|---|---|---|---|
T1 |
As-spun |
2.82 × 10−3 (1.44 × 10−3) |
–3.11–8.73 |
103–105 |
80 |
4.11 × 10−3 (1.76 × 10−3) |
7.18–14.67 |
103–105 |
|
120 |
2.27 × 10−3 (1.52 × 10−3) |
14.70–18.33 |
103–105 |
|
T2 |
As-spun |
0.27 × 10−3 (0.19 × 10−3) |
2.22–13.37 |
102–104 |
80 |
0.39 × 10−3 (0.20 × 10−3) |
1.57–6.43 |
102–104 |
|
120 |
0.15 × 10−3 (0.12 × 10−3) |
4.13–6.10 |
102–104 |
a The performance data were obtained based on at least 10 different devices.
To investigate the different device performances of T1 and T2, the surface morphologies, crystallinity, and microstructures of the thin films of T1 and T2 were analyzed by using atomic force microscopy (AFM) and X-ray diffraction (XRD), which play an important role in affecting the electronic properties.[4] [30] [Figure 4] shows the AFM images of the as-spun and annealed thin films of T1 ([Figure 4a–c]) and T2 ([Figure 4d–f]) deposited on an OTS-modified Si/SiO2 substrate, respectively. T1 exhibited a much smoother and uniform film morphology with a very small root-mean-square (RMS) surface roughness of about 1 nm compared to that of T2 (RMS values of 2.46–4.63 nm), which is beneficial for charge accumulation and transport in the conducting channel and might account for the better electron-transporting property of T1. Moreover, the thin films of T1 display no appreciable change (RMS values of 1.02–0.80 nm) upon annealing at 80 °C and 120 °C, respectively. In contrast, the surface morphologies of T2 were changed drastically with large and discontinuous domains (RMS value of up to 4.63 nm) after thermal annealing as shown in [Figure 4f]. Such high surface roughness and large domain boundaries of T2-based thin films are deleterious for electron transport.[25b] [30] The XRD images of T1- and T2-based thin films showed no apparent diffraction peaks even after high-temperature thermal annealing ([Figure S4]), suggesting their randomly arranged packing on the substrate.[31]
Finally, the potential of rhodanine-embedded NDI2DT-DTYM2 as non-fullerene ETM in PSC devices was investigated. We first evaluated the electron motilities of T2 and NDI2DT-DTYM2 using the space-charge-limited current (SCLC) method with a device configuration of ITO/ZnO/T2 (or NDI2DT-DTYM2)/Al. T2 showed a SCLC electron mobility of 2.72 × 10−4 cm2 V−1 s−1, which is about 1 order of magnitude higher than that of NDI2DT-DTYM2 (2.64 × 10−5 cm2 V−1 s−1, [Figure S6]). For T2, in consideration of its high electron charge transport in the vertical direction, better solubility in common organic solvents, and the LUMO energy level's well alignment with the conducting band minimum of MAPbI3,[10] [15a] PSC devices using T2 as ETMs with the inverted structure of ITO/PTAA/MAPbI3/T2(or NDI2DT-DTYM2)/BCP/Ag were fabricated. [Figures 5] and [S7] depict the representative current density–voltage (J–V) curve and external quantum efficiency (EQE) spectra of T2- or NDI2DT-DYTM2-based PSCs, respectively, and the corresponding performance parameters of PSCs are collected in [Table S1]. The PSC devices with T2 as the ETMs produced a J sc, V oc, and PCE value of 20.43 mA cm−2, 0.91 V, and 8.82%, respectively, which are slight higher than those of NDI2DT-DTYM2-based PSCs ([Table S1]). The inverted PSC devices using T2 as ETMs showed an EQE response from 300 to 800 nm with the maximum value of 81.7%, and the integrated J sc of 18.14 mA cm−2 was obtained from the EQE curve.
#
Conclusions
In summary, T1 and T2 have been designed and efficiently synthesized via an effective strategy that incorporated a rhodanine unit into the core-expanded NDI2DT-DTYM2 backbone. Compared to NDI2DT-DTYM2, both T1 and T2 showed higher LUMO energy levels (< − 4.20 eV) and lower optical band gaps (ca. 1.5 eV), demonstrating that rhodanine units play a significant role in tuning the optical and electronic properties of T1 and T2. The OTFT devices based on T1 and T2 exhibit n-type semiconducting properties with μ e of about10−3 cm2 V−1 s−1, and the inverted PSC devices using T2 as ETMs displayed a decent J sc, V oc, and PCE value of 20.43 mA cm−2, 0.91 V, and 8.82%, respectively. The above results indicate that the core-extended strategy by embedding a rhodanine unit into the backbone of OSCs is applicable and promising for constructing new families of high performance n-type semiconductors with multifunctional applications.
#
Experimental Section
Materials and General Method
1,4,5,8-NDA, DBH, PBr3, H2SO4, malononitrile, octyl isothiocyanate, and A4 were purchased from Shanghai Aldrich and used as received. THF was dried using sodium and freshly distilled prior to use. CH3NH2 was obtained from Energy Chemical, China. HI, 55–58 wt% in water, was purchased from Aladdin, China. Bathocuproine (BCP) was purchased from TCI, Japan. Dimethylsulphoxide (DMSO) and N,N-dimethylformamide (DMF) were obtained from J & K, China. Indium tin oxide-coated(ITO) glasses were purchased from Kaivo, China. Aluminum (Al) was purchased from Cuibolin, China. Silver (Ag) was purchased from CNM, China. 1H NMR (400 MHz) and 13C NMR (100 MHz) spectra were measured in deuterated chloroform (CDCl3) on JEOL RESONANCE ECZ 400S instruments. Mass spectra (MALDI-TOF) were recorded on a Voyager-DE STR mass spectrometer. Elemental analyses were carried out on an Elementar Vario EL III elemental analyzer. TGA measurements were performed on a TA Q500 instrument under a dry nitrogen flow at a heating rate of 10 °C/min, heating from room temperature to 500 °C. DSC analyses were carried out on a Perkin Elmer Pyris 1 instrument under a dry N2 flow at a heating rate of 10 °C/min, heating from room temperature to 350 °C. The electrochemical measurements for T1, T2, and NDI2DT-DTYM2 were performed on a CHI610D electrochemical work station in a conventional three-electrode cell using a platinum working electrode, a platinum-wire auxiliary electrode, and a saturated calomel electrode (SCE) reference electrode in a solution of [Bu4N][PF6] (0.1 M) in CHCl3 at a scan rate of 100 mV/s. The experiments were calibrated with the standard ferrocene/ferrocenium (F c) redox system and assumption that the energy level of F c is 4.8 eV below vacuum. Optical absorption was measured on a JASCO V-570 UV-vis-NIR spectrophotometer. XRD measurements were carried out in the reflection mode with Cu Kα radiation using a Panalytical X'Pert Pro XRD system. AFM was recorded on a JPK atomic force microscope by an AC mode with a silicon tip. The current density–voltage (J–V) characteristics of the devices were measured with a Keithley 2420 measurement source unit maintained at room temperature in a N2-filled glovebox. Photocurrent was acquired upon irradiation using an AAA solar simulator (Oriel 94043A, 450 W, USA) with an AM 1.5 G filter. Light intensity was simulated to be 100 mW cm−2 using a NREL-certified standard silicon cell (Oriel reference cell 91150, USA). EQE was measured with a 75 W xenon lamp that was equipped with an Oriel monochromator (74125), an optical chopper, a lock-in amplifier, and an NREL-calibrated crystalline silicon cell.
#
Device Fabrication and Characterization
OTFT device fabrication and characterization: The OTFT devices based on T1 and T2 were fabricated by a spin-coating method with a bottom-gate top-contact (BG/TC) configuration with a channel length of 31 μm and a width of 273 μm. The Si/SiO2 substrates were cleaned via a standard procedure. The Si/SiO2 substrates were modified with octadecyltrichlorosilane (OTS) on the surface via a vapor deposition method for about 4 hours. Then, the substrates were rinsed with chloroform, n-hexane, acetone, and isopropyl alcohol subsequently by ultrasonic cleaning for 5 min, respectively. Then, the Si/SiO2 substrate was dried with N2 quickly. The active layers were fabricated on the OTS-treated substrate by spin-coating with the small-molecule solutions in chlorobenzene for T1 (5 mg mL−1) and in chloroform for T2 (10 mg mL−1), respectively. Finally, Au was used as a source and drain electrode, and was deposited on the top of the semiconducting layer through a shadow mask under high vacuum. The device performances were measured with a Keithley 4200 semiconductor parameter analyzer. The mobilities were calculated from the equation: I DS = (μWC i/2L)(V GS − V T)2, where I DS is the source-drain current, μ is the carrier mobility, C i is the capacitance per unit area of the dielectric layer (10 nF/cm2), V GS and V T are the gate voltage and threshold voltage, respectively.
PSCs device fabrication and characterization: ITO glass was cleaned using detergent, deionized water, acetone, and isopropanol ultrasonic baths step by step for 20 min before drying in a N2 flow, respectively. Then the ITO substrate was cleaned by ultraviolet ozone (UVO) for 20 min. A thin layer of PTAA was spin-coated onto the cleaned ITO at 4000 rpm for 60 s, and annealed at 140 °C for 15 min. Finally the ITO-coated substrates were transferred into a N2-filled glovebox for active layer deposition and further device fabrication. The active layer was deposited via a two-step procedure: first step: a precursor mixture solution with PbI2: MAI = 1.3: 0.3 M in a mixture of DMF and DMSO (9:1, v:v); second step: a solution with MAI 55 mg/mL in isopropanol (IPA) was spin-coated onto the PTAA-coated-ITO (ITO-PTAA) substrate at 1000 rpm for 10 s and 4000 rpm for 50 s, respectively, and then annealed at 90 °C for 30 min. After cooling of the PSC active layer to room temperature, the T2 (10 mg/mL) and BCP (0.5 mg/mL in IPA) solutions were used to deposit subsequently at 1000 rpm for 30 s and 4000 rpm for 40 s at room temperature, respectively. Finally, 100 nm of Ag film was thermal evaporated as counter electrodes using a shadow mask to finish the device fabrication process. The accurate active cell area of the device by the overlap of the electrodes was about 0.04 cm2. The J–V characteristics of the PSCs were measured with a Keithley 2420 measurement source unit maintained at room temperature in the N2-filled glovebox. Photocurrent was acquired upon irradiation using an AAA solar simulator (Oriel 94043A, 450 W, USA) with an AM 1.5 G filter. Light intensity was simulated to be 100 mW/cm2 using an NREL-certified standard silicon cell (Oriel reference cell 91150, USA). EQE was measured with a 75 W xenon lamp that was equipped with an Oriel monochromator (74125), an optical chopper, a lock-in amplifier, and an NREL-calibrated crystalline silicon cell.
#
Synthetic Part
Compound T1: Under a nitrogen atmosphere, a solution of CS2 in THF was added slowly to NaH (120 mg, w = 60%, 3 mmol) at 0 °C, and then stirred at room temperature for 4 hours. The mixture was added to A3 solution (125.5 mg, 0.1 mmol) and stirred at room temperature for another 1 hour. After the reaction was completed, some water was added to the mixture and extracted with chloroform. The combined organic layer was dried using Na2SO4 and the filtrate was concentrated under reduced pressure. Chromatography of the residue on a silica gel column with dichloromethane/petroleum ether (1/1) as an eluent afforded T1 as a bluish green solid (120 mg, yield: 51.2%). Mp > 300 °C. 1H NMR (400 MHz, CDCl3) δ 4.35 (dd, J = 13.2, 6.2 Hz, 4H), 4.27 (d, J = 7.2 Hz, 4H), 2.07 (d, J = 4.1 Hz, 2H), 1.48 (t, J = 5.9 Hz, 6H), 1.39–1.15 (m, 80H), 0.89–0.81 (m, 12H). 13C NMR (100 MHz, CDCl3) δ = 165.98, 165.16, 164.94, 150.72, 150.30, 145.85, 128.37, 119.60, 44.48, 39.71, 34.87, 33.11, 32.67, 29.57, 25.59, 16.98. FT-IR (KBr): 2922.5, 2851.6, 2216.4, 1694.6, 1636.9, 1526.1, 1457.1, 1388.5, 1375.1, 1338.1, 1295.1, 1212.7, 1088.8, 1070.3, 882.5, 837.1, 784.0, 739.0, 726.8, 693.3, 630.7, 547.0, 503.7, 461.5 cm−1. MS (MALDI-TOF) m/z: 1469.6716 (M + H)+; HR-MS (MALDI-TOF) (M + H)+ calcd for C80H108N8O6S6: 1469.6716; found: 1469.6788. Anal. calcd. for C80H108N8O6S6 (%): C, 65.36; H, 7.40; N, 7.62; found: C, 65.53; H, 7.50; N, 7.58.
Compound T2: A similar synthesis and purification method to T1 was implemented for the preparation of T2 (220 mg, yield 67.2%), by using A5 instead of A4. Mp > 300 °C. 1H NMR (400 MHz, CDCl3) δ 4.26 (dd, J = 13.3, 6.6 Hz, 8H), 2.06 (ddd, J = 18.3, 13.1, 5.6 Hz, 2H), 1.46–1.17 (m, 104H), 0.92–0.82 (m, 18H). 13C NMR (100 MHz, CDCl3) δ = 163.02, 162.06, 161.77, 117.02, 111.89, 46.20, 36.61, 31.93, 31.75, 31.61, 30.19, 29.71, 29.38, 29.11, 26.29, 22.66, 14.11. FT-IR (KBr): 2921.1, 2851.6, 2214.8, 1733.1, 1716.6, 1694.4, 1652.6, 1636.2, 1526.5, 1506.8, 1456.4, 1385.0, 1338.3, 1295.3, 1209.6, 1167.4, 829.2, 784.0, 739.4, 632.9, 580.8, 418.8 cm−1. LRMS: (MALDI-TOF) (M + H)+ calcd for C92H132N8O6S6: 1638.8628; found: 1638.3. Anal. calcd. for C92H132N8O6S6 (%): C, 67.44; H, 8.12; N, 6.84; found: C, 67.46; H, 7.94; N, 6.72.
#
#
#
No conflict of interest has been declared by the author(s).
Supporting Information
Supporting information for this article is available online at http://doi.org/10.1055/s-0040-1710550.
-
References
- 1a Dong H, Fu X, Liu J, Wang Z, Hu W. Adv. Mater. 2013; 25: 6158
- 1b Dennler G, Scharber M, Brabec C. Adv. Mater. 2009; 21: 1323
- 1c Yang Z, Mao Z, Xie Z, Zhang Y, Liu S, Zhao J, Xu J, Chi Z. Chem. Soc. Rev. 2017; 46: 915
- 1d Han S, Peng H, Sun Q, Venkatesh S, Chung K, Lau S, Zhou Y, Roy V. Adv. Mater. 2017; 29: 1700375
- 1e Zaumseil J, Sirringhaus H. Chem. Rev. 2007; 107: 1296
- 1f Murphy AR, Fréchet JM. Chem. Rev. 2007; 107: 1066
- 1g Usta H, Facchetti A, Marks TJ. Acc. Chem. Res. 2011; 44: 501
- 1h Klauk H. Chem. Soc. Rev. 2010; 39: 2643
- 1i Torrent M, Rovira C. Chem. Soc. Rev. 2008; 37: 827
- 2a Wang C, Dong H, Hu W, Liu Y, Zhu D. Chem. Rev. 2012; 112: 2208
- 2b Mandal S, Noh YY. Semicond. Sci. Technol. 2015; 30: 064003
- 2c Tong S, Sun J, Yang J. ACS Appl. Mater. Interfaces 2018; 10: 25902
- 3a Yu Y, Ma Q, Ling H, Li W, Ju R, Bian L, Shi N, Qian Y, Yi M, Xie L, Huang W. Adv. Funct. Mater. 2019; 29: 1904602
- 3b Sui Y, Deng YF, Du T, Shi Y, Geng Y. Mater. Chem. Front. 2019; 3: 1932
- 3c Ren Y, Yang X, Zhou L, Mao J, Han S, Zhou Y. Adv. Funct. Mater. 2019; 29: 1902105
- 4a Di CA, Zhang F, Zhu D. Adv. Mater. 2013; 25: 313
- 4b Zhang F, Di CA, Berdunov N, Hu Y, Hu YB, Gao X, Meng Q, Sirringhaus H, Zhu D. Adv. Mater. 2013; 25: 1401
- 4c Zhao Y, Di CA, Gao X, Hu Y, Guo Y, Zhang L, Liu Y, Wang J, Hu W, Zhu D. Adv. Mater. 2011; 23: 2448
- 5a Gao X, Di CA, Hu Y, Yang X, Fan H, Zhang F, Liu Y, Li H, Zhu D. J. Am. Chem. Soc. 2010; 132: 3697
- 5b Minemawari H, Yamada T, Matsui H, Tsutsumi J, Haas S, Chiba R, Kumai R, Hasegawa T. Nature 2011; 475: 364
- 5c Zhang F, Di CA, Berdunov N, Hu Y, Gao X, Meng Q, Sirringhaus H, Zhu D. Adv. Mater. 2013; 25: 1401
- 6a Sokolov AN, Tee BC, Bettinger CJ, Tok JB, Bao Z. Acc. Chem. Res. 2012; 45: 361
- 6b Nakayama K, Hirose Y, Soeda J, Yoshizumi M, Uemura T, Uno M, Li W, Kang M, Yamagishi M, Okada Y, Miyazaki E, Nakazawa Y, Nakao A, Takimiya K, Takeya J. Adv. Mater. 2011; 23: 1626
- 7a Someya T, Dodabalapur A, Huang J, See KC, Katz HE. Adv. Mater. 2010; 22: 3799
- 7b Li H, Shi W, Song J, Jang H, Dailey J, Yu J, Katz H. Chem. Rev. 2019; 119: 3
- 8a Marrocchi A, Facchetti A, Lanari D, Petruccia C, Vaccaro L. Energy Environ. Sci. 2016; 9: 763
- 8b Bohra H, Wang M. J. Mater. Chem. A 2017; 5: 11550-1
- 8c Gu P, Wang N, Wang C, Zhou Y, Long G, Tian M, Chen W, Sun X, Kanatzidis M, Zhang Q. J. Mater. Chem. A 2017; 5: 7339
- 8d Wang N, Zhao K, Ding T, Liu W, Ahmed A, Wang Z, Tian M, Sun X, Zhang Q. Adv. Energy Mater. 2017; 7: 1700522
- 9a Pandey L, Risko C, Norton J, Bredas J. Macromolecules 2012; 45: 6405
- 9b Usta H, Facchetti A, Marks TJ. J. Am. Chem. Soc. 2008; 130: 8580
- 10a Tian J, Xue Q, Tang X, Chen Y, Li N, Hu Z, Yip HL. Adv. Mater. 2019; 31: 1901152
- 10b Ye Q, Zhao Y, Mu S, Ma F, Gao F, Chu Z, Yin Z, Gao P, Zhang X, You J. Adv. Mater. 2019; 31: 1905143
- 10c Said A, Xie J, Zhang Q. Small 2019; 15: 1900854
- 11a Cheng YJ, Yang SH, Hsu CS. Chem. Rev. 2009; 109: 5868
- 11b Lu D, Yang X, Leng B, Yang X, Ge C, Jia X, Gao X. Chin. Chem. Lett. 2016; 27: 1022
- 12a Hu Y, Gao X, Di C, Yang X, Zhang F, Liu Y, Li H, Zhu D. Chem. Mater. 2011; 23: 1204
- 12b Zhao Y, Di CA, Gao X, Hu Y, Guo Y, Zhang L, Liu Y, Wang J, Hu W, Zhu D. Adv. Mater. 2011; 23: 2448
- 12c Wu W, Li J, Zhao Z, Yang X, Gao X. Org. Chem. Front. 2017; 4: 823
- 13a Suraru SL, Zschieschang U, Klauk H, Würthner F. Chem. Commun. 2011; 47: 11504
- 13b Suraru SL, Burschka C, Würthner F. J. Org. Chem. 2014; 79: 128
- 13c Gao X, Hu Y. J. Mater. Chem. C 2014; 2: 3099-3117
- 14a Kobaisi MA, Bhosale SV, Latham K, Raynor AM, Bhosale SV. Chem. Rev. 2016; 116: 11685
- 14b Guo X, Facchetti A, Marks TJ. Chem. Rev. 2014; 114: 8943
- 15a Ge C, , W W, Hu L, Hu Y, Zhou Y, Li W, Gao X. Org. Electron. 2018; 61: 113
- 15b Nakamura T, Shioya N, Shimoaka T, Nishikubo R, Hasegawa T, Saeki A, Murata Y, Murdey R, Wakamiya A. Chem. Mater. 2019; 31: 1729
- 16a Katz H, Johnson J, Lovinger A, Li W. J. Am. Chem. Soc. 2000; 122: 7787
- 16b Shukla D, Nelson S, Freeman D, Rajeswaran M, Ahearn W, Meyer D, Carey J. Chem. Mater. 2008; 20: 7486
- 16c Luo H, Liu Z, Cai Z, Wu L, Zhang G, Liu C, Zhang D. Chin. J. Chem. 2012; 30: 1453
- 17a Hu Y, Qin Y, Gao X, Zhang F, Di C, Zhao Z, Li H, Zhu D. Org. Lett. 2012; 14: 292
- 17b Katz HE, Lovinger AJ, Johnson J, Kloc C, Siegrist T, Li W, Lin Y, Dodabalapur A. Nature 2000; 404: 478
- 18a Suraru S, Würthner F. Angew. Chem. Int. Ed. 2014; 53: 7428
- 18b Fan W, Liu C, Li Y, Wang Z. Chem. Commun. 2016; 53: 188
- 19a Kim R, Amegadze P, Kang I, Yun H, Noh Y, Kwon S, Kim Y. Adv. Funct. Mater. 2013; 23: 5719
- 19b Liu Z, Zhang G, Cai Z, Chen X, Luo H, Li Y, Wang J, Zhang D. Adv. Mater. 2014; 26: 6965
- 19c Gsänger M, Bialas D, Huang L, Stolte M, Würthner F. Adv. Mater. 2016; 28: 3615
- 20a Chen Z, Zheng Y, Yan H, Facchetti A. J. Am. Chem. Soc. 2009; 131: 8
- 20b Yan H, Chen Z, Zheng Y, Newman C, Quinn J, Dotz F, Kastler M, Facchetti A. Nature 2009; 457: 679
- 20c Tachapermpon Y, Maniam S, Wanichacheva N, Langford S. Asian J. Org. Chem. 2017; 6: 47
- 21a Jones B, Facchetti A, Marks T, Wasielewski M. Chem. Mater. 2007; 19: 2703
- 21b Nakano M, Osaka I, Hashizume D, Takimiya K. Chem. Mater. 2015; 27: 6418
- 21c Sakai N, Mareda J, Vauthey E, Matile S. Chem. Commun. 2010; 46: 4225
- 22a Fukutomi Y, Nakano M, Hu JY, Osaka I, Takimiya K. J. Am. Chem. Soc. 2013; 135: 11445
- 22b Fan W, Winands T, Doltsinis NL, Li Y, Wang Z. Angew. Chem. Int. Ed. 2017; 56: 15373
- 22c Cui X, Xiao C, Winands T, Koch T, Li Y, Zhang L, Doltsinis NL, Wang Z. J. Am. Chem. Soc. 2018; 140: 12175
- 23a Tan L, Guo Y, Zhang G, Yang Y, Zhang D, Yu G, Xu W, Liu Y. J. Mater. Chem. 2011; 21: 18042
- 23b Suraru SL, Würthner F. J. Org. Chem. 2013; 78: 5227
- 23c Insuasty A, Maniam S, Langford SJ. Chemistry 2019; 25: 7058
- 23d Li C, Xiao C, Li Y, Wang Z. Org. Lett. 2013; 15: 682
- 24 Liu H, Li Z, Zhao D. Sci. China Mater. 2019; 62: 1574
- 25a Sasikumar M, Suseela YV, Govindaraju T. Asian J. Org. Chem. 2013; 2: 779
- 25b Gao X, Qiu W, Yang X, Liu Y, Wang Y, Zhang H, Qi T, Liu Y, Lu K, Du C, Shuai Z, Yu G, Zhu D. Org. Lett. 2007; 9: 3917
- 25c Zhao Z, Zhang F, Hu Y, Wang Z, Leng B, Gao X, Di C, Zhu D. ACS Macro Lett. 2014; 3: 1174
- 26 Luo HW, Cai Z, Tan L, Guo Y, Yang G, Liu Z, Zhang G, Zhang D, Xu W, Liu Y. J. Mater. Chem. C 2013; 1: 2688
- 27 Wu H, Wang Y, Qiao X, Wang D, Yang X, Li H. Chem. Mater. 2018; 30: 6992
- 28a Spano FC. Acc. Chem. Res. 2010; 43: 429
- 28b Montoya M, Janssen R. Adv. Funct. Mater. 2017; 27: 1605779
- 28c Yi Y, Feng H, Zheng N, Ke X, Kan B, Chang M, Xie Z, Wan X, Li C, Chen Y. Chem. Mater. 2019; 31: 904
- 29a Dou L, Gao J, Richard E, You J, Chen C, Cha K, He Y, Li G, Yang Y. J. Am. Chem. Soc. 2012; 134: 10071
- 29b Chen X, Guo Y, Tan L, Yang G, Li Y, Zhang G, Liu Z, Xu W, Zhang D. J. Mater. Chem. C 2013; 1: 1087
- 30a Di CA, Liu Y, Yu G, Zhu D. Acc. Chem. Res. 2009; 42: 1573
- 30b Dong H, Jiang L, Hu W. Phys. Chem. Chem. Phys. 2012; 14: 14165
- 30c Pujari S, Scheres L, Marcelis A, Zuilhof H. Angew. Chem. Int. Ed. 2014; 53: 6322
- 30d Magliulo M, Manoli K, Macchia E, Palazzo G, Torsi L. Adv. Mater. 2015; 27: 7528
-
References
- 1a Dong H, Fu X, Liu J, Wang Z, Hu W. Adv. Mater. 2013; 25: 6158
- 1b Dennler G, Scharber M, Brabec C. Adv. Mater. 2009; 21: 1323
- 1c Yang Z, Mao Z, Xie Z, Zhang Y, Liu S, Zhao J, Xu J, Chi Z. Chem. Soc. Rev. 2017; 46: 915
- 1d Han S, Peng H, Sun Q, Venkatesh S, Chung K, Lau S, Zhou Y, Roy V. Adv. Mater. 2017; 29: 1700375
- 1e Zaumseil J, Sirringhaus H. Chem. Rev. 2007; 107: 1296
- 1f Murphy AR, Fréchet JM. Chem. Rev. 2007; 107: 1066
- 1g Usta H, Facchetti A, Marks TJ. Acc. Chem. Res. 2011; 44: 501
- 1h Klauk H. Chem. Soc. Rev. 2010; 39: 2643
- 1i Torrent M, Rovira C. Chem. Soc. Rev. 2008; 37: 827
- 2a Wang C, Dong H, Hu W, Liu Y, Zhu D. Chem. Rev. 2012; 112: 2208
- 2b Mandal S, Noh YY. Semicond. Sci. Technol. 2015; 30: 064003
- 2c Tong S, Sun J, Yang J. ACS Appl. Mater. Interfaces 2018; 10: 25902
- 3a Yu Y, Ma Q, Ling H, Li W, Ju R, Bian L, Shi N, Qian Y, Yi M, Xie L, Huang W. Adv. Funct. Mater. 2019; 29: 1904602
- 3b Sui Y, Deng YF, Du T, Shi Y, Geng Y. Mater. Chem. Front. 2019; 3: 1932
- 3c Ren Y, Yang X, Zhou L, Mao J, Han S, Zhou Y. Adv. Funct. Mater. 2019; 29: 1902105
- 4a Di CA, Zhang F, Zhu D. Adv. Mater. 2013; 25: 313
- 4b Zhang F, Di CA, Berdunov N, Hu Y, Hu YB, Gao X, Meng Q, Sirringhaus H, Zhu D. Adv. Mater. 2013; 25: 1401
- 4c Zhao Y, Di CA, Gao X, Hu Y, Guo Y, Zhang L, Liu Y, Wang J, Hu W, Zhu D. Adv. Mater. 2011; 23: 2448
- 5a Gao X, Di CA, Hu Y, Yang X, Fan H, Zhang F, Liu Y, Li H, Zhu D. J. Am. Chem. Soc. 2010; 132: 3697
- 5b Minemawari H, Yamada T, Matsui H, Tsutsumi J, Haas S, Chiba R, Kumai R, Hasegawa T. Nature 2011; 475: 364
- 5c Zhang F, Di CA, Berdunov N, Hu Y, Gao X, Meng Q, Sirringhaus H, Zhu D. Adv. Mater. 2013; 25: 1401
- 6a Sokolov AN, Tee BC, Bettinger CJ, Tok JB, Bao Z. Acc. Chem. Res. 2012; 45: 361
- 6b Nakayama K, Hirose Y, Soeda J, Yoshizumi M, Uemura T, Uno M, Li W, Kang M, Yamagishi M, Okada Y, Miyazaki E, Nakazawa Y, Nakao A, Takimiya K, Takeya J. Adv. Mater. 2011; 23: 1626
- 7a Someya T, Dodabalapur A, Huang J, See KC, Katz HE. Adv. Mater. 2010; 22: 3799
- 7b Li H, Shi W, Song J, Jang H, Dailey J, Yu J, Katz H. Chem. Rev. 2019; 119: 3
- 8a Marrocchi A, Facchetti A, Lanari D, Petruccia C, Vaccaro L. Energy Environ. Sci. 2016; 9: 763
- 8b Bohra H, Wang M. J. Mater. Chem. A 2017; 5: 11550-1
- 8c Gu P, Wang N, Wang C, Zhou Y, Long G, Tian M, Chen W, Sun X, Kanatzidis M, Zhang Q. J. Mater. Chem. A 2017; 5: 7339
- 8d Wang N, Zhao K, Ding T, Liu W, Ahmed A, Wang Z, Tian M, Sun X, Zhang Q. Adv. Energy Mater. 2017; 7: 1700522
- 9a Pandey L, Risko C, Norton J, Bredas J. Macromolecules 2012; 45: 6405
- 9b Usta H, Facchetti A, Marks TJ. J. Am. Chem. Soc. 2008; 130: 8580
- 10a Tian J, Xue Q, Tang X, Chen Y, Li N, Hu Z, Yip HL. Adv. Mater. 2019; 31: 1901152
- 10b Ye Q, Zhao Y, Mu S, Ma F, Gao F, Chu Z, Yin Z, Gao P, Zhang X, You J. Adv. Mater. 2019; 31: 1905143
- 10c Said A, Xie J, Zhang Q. Small 2019; 15: 1900854
- 11a Cheng YJ, Yang SH, Hsu CS. Chem. Rev. 2009; 109: 5868
- 11b Lu D, Yang X, Leng B, Yang X, Ge C, Jia X, Gao X. Chin. Chem. Lett. 2016; 27: 1022
- 12a Hu Y, Gao X, Di C, Yang X, Zhang F, Liu Y, Li H, Zhu D. Chem. Mater. 2011; 23: 1204
- 12b Zhao Y, Di CA, Gao X, Hu Y, Guo Y, Zhang L, Liu Y, Wang J, Hu W, Zhu D. Adv. Mater. 2011; 23: 2448
- 12c Wu W, Li J, Zhao Z, Yang X, Gao X. Org. Chem. Front. 2017; 4: 823
- 13a Suraru SL, Zschieschang U, Klauk H, Würthner F. Chem. Commun. 2011; 47: 11504
- 13b Suraru SL, Burschka C, Würthner F. J. Org. Chem. 2014; 79: 128
- 13c Gao X, Hu Y. J. Mater. Chem. C 2014; 2: 3099-3117
- 14a Kobaisi MA, Bhosale SV, Latham K, Raynor AM, Bhosale SV. Chem. Rev. 2016; 116: 11685
- 14b Guo X, Facchetti A, Marks TJ. Chem. Rev. 2014; 114: 8943
- 15a Ge C, , W W, Hu L, Hu Y, Zhou Y, Li W, Gao X. Org. Electron. 2018; 61: 113
- 15b Nakamura T, Shioya N, Shimoaka T, Nishikubo R, Hasegawa T, Saeki A, Murata Y, Murdey R, Wakamiya A. Chem. Mater. 2019; 31: 1729
- 16a Katz H, Johnson J, Lovinger A, Li W. J. Am. Chem. Soc. 2000; 122: 7787
- 16b Shukla D, Nelson S, Freeman D, Rajeswaran M, Ahearn W, Meyer D, Carey J. Chem. Mater. 2008; 20: 7486
- 16c Luo H, Liu Z, Cai Z, Wu L, Zhang G, Liu C, Zhang D. Chin. J. Chem. 2012; 30: 1453
- 17a Hu Y, Qin Y, Gao X, Zhang F, Di C, Zhao Z, Li H, Zhu D. Org. Lett. 2012; 14: 292
- 17b Katz HE, Lovinger AJ, Johnson J, Kloc C, Siegrist T, Li W, Lin Y, Dodabalapur A. Nature 2000; 404: 478
- 18a Suraru S, Würthner F. Angew. Chem. Int. Ed. 2014; 53: 7428
- 18b Fan W, Liu C, Li Y, Wang Z. Chem. Commun. 2016; 53: 188
- 19a Kim R, Amegadze P, Kang I, Yun H, Noh Y, Kwon S, Kim Y. Adv. Funct. Mater. 2013; 23: 5719
- 19b Liu Z, Zhang G, Cai Z, Chen X, Luo H, Li Y, Wang J, Zhang D. Adv. Mater. 2014; 26: 6965
- 19c Gsänger M, Bialas D, Huang L, Stolte M, Würthner F. Adv. Mater. 2016; 28: 3615
- 20a Chen Z, Zheng Y, Yan H, Facchetti A. J. Am. Chem. Soc. 2009; 131: 8
- 20b Yan H, Chen Z, Zheng Y, Newman C, Quinn J, Dotz F, Kastler M, Facchetti A. Nature 2009; 457: 679
- 20c Tachapermpon Y, Maniam S, Wanichacheva N, Langford S. Asian J. Org. Chem. 2017; 6: 47
- 21a Jones B, Facchetti A, Marks T, Wasielewski M. Chem. Mater. 2007; 19: 2703
- 21b Nakano M, Osaka I, Hashizume D, Takimiya K. Chem. Mater. 2015; 27: 6418
- 21c Sakai N, Mareda J, Vauthey E, Matile S. Chem. Commun. 2010; 46: 4225
- 22a Fukutomi Y, Nakano M, Hu JY, Osaka I, Takimiya K. J. Am. Chem. Soc. 2013; 135: 11445
- 22b Fan W, Winands T, Doltsinis NL, Li Y, Wang Z. Angew. Chem. Int. Ed. 2017; 56: 15373
- 22c Cui X, Xiao C, Winands T, Koch T, Li Y, Zhang L, Doltsinis NL, Wang Z. J. Am. Chem. Soc. 2018; 140: 12175
- 23a Tan L, Guo Y, Zhang G, Yang Y, Zhang D, Yu G, Xu W, Liu Y. J. Mater. Chem. 2011; 21: 18042
- 23b Suraru SL, Würthner F. J. Org. Chem. 2013; 78: 5227
- 23c Insuasty A, Maniam S, Langford SJ. Chemistry 2019; 25: 7058
- 23d Li C, Xiao C, Li Y, Wang Z. Org. Lett. 2013; 15: 682
- 24 Liu H, Li Z, Zhao D. Sci. China Mater. 2019; 62: 1574
- 25a Sasikumar M, Suseela YV, Govindaraju T. Asian J. Org. Chem. 2013; 2: 779
- 25b Gao X, Qiu W, Yang X, Liu Y, Wang Y, Zhang H, Qi T, Liu Y, Lu K, Du C, Shuai Z, Yu G, Zhu D. Org. Lett. 2007; 9: 3917
- 25c Zhao Z, Zhang F, Hu Y, Wang Z, Leng B, Gao X, Di C, Zhu D. ACS Macro Lett. 2014; 3: 1174
- 26 Luo HW, Cai Z, Tan L, Guo Y, Yang G, Liu Z, Zhang G, Zhang D, Xu W, Liu Y. J. Mater. Chem. C 2013; 1: 2688
- 27 Wu H, Wang Y, Qiao X, Wang D, Yang X, Li H. Chem. Mater. 2018; 30: 6992
- 28a Spano FC. Acc. Chem. Res. 2010; 43: 429
- 28b Montoya M, Janssen R. Adv. Funct. Mater. 2017; 27: 1605779
- 28c Yi Y, Feng H, Zheng N, Ke X, Kan B, Chang M, Xie Z, Wan X, Li C, Chen Y. Chem. Mater. 2019; 31: 904
- 29a Dou L, Gao J, Richard E, You J, Chen C, Cha K, He Y, Li G, Yang Y. J. Am. Chem. Soc. 2012; 134: 10071
- 29b Chen X, Guo Y, Tan L, Yang G, Li Y, Zhang G, Liu Z, Xu W, Zhang D. J. Mater. Chem. C 2013; 1: 1087
- 30a Di CA, Liu Y, Yu G, Zhu D. Acc. Chem. Res. 2009; 42: 1573
- 30b Dong H, Jiang L, Hu W. Phys. Chem. Chem. Phys. 2012; 14: 14165
- 30c Pujari S, Scheres L, Marcelis A, Zuilhof H. Angew. Chem. Int. Ed. 2014; 53: 6322
- 30d Magliulo M, Manoli K, Macchia E, Palazzo G, Torsi L. Adv. Mater. 2015; 27: 7528