Pyrene-Based Macrocrosslinkers with Supramolecular Mechanochromism for Elastic Deformation Sensing in Hydrogel Networks
Abstract
Excimer-containing polymers with supramolecular mechanochromism are an attractive and well-investigated class of mechanoresponsive materials. However, only recently steps toward mechanophore-like mechanochromic systems that are anchored within the parent polymer structure and that show defined optical transitions on the molecular scale have been reported. However, the multi-step syntheses of these constructs are tedious. Here we report the development of a series of pyrene-based macrocrosslinkers that display supramolecular mechanochromism and are readily synthesized from mostly commercial reagents. We incorporate the water-soluble macrocrosslinkers in hydrogel networks and demonstrate their reversible mechanochromic behavior in the elastic deformation regime.
#
Introduction
Pyrene is a well-established fluorophore[1] that is commonly used because of its ability to form excimers, long excited-state lifetime,[2] high fluorescence quantum yield, and good photostability.[3] Excimer formation is a diffusion-controlled process that leads to a bathochromically shifted emission when a pyrene in the ground state binds to a pyrene in the excited state.[4] Hence, excimer emission strongly depends on the distance between the excimer-forming molecules rendering pyrene a popular distance-based probe in applications ranging from organic electronics[5] to sensors for temperature,[6] pH,[7] pressure,[8] small molecules,[9] protein conformation,[10] lipid structure,[11] or nucleic acid recognition.[12]
The strong distance sensitivity of excimer systems is particularly attractive for the visualization of stress and strain in bulk polymer materials.[13]–[15] Weder and coworkers have pioneered early research in this field focusing on blending excimer-forming dyes in polymer films.[16] Yet, this has led to only a weak correlation between mechanical polymer deformation and the measured optical signal. While these systems hence have allowed the qualitative observation of force-induced effects, polymer-anchored mechanophore-like[17],[18] systems have only recently been developed that enable the visualization of discrete force-induced molecular events despite the absence of a clear bond dissociation reaction. For example, emitter–quencher pairs have been bridged and anchored within rotaxanes[19]–[22] and cyclophanes,[23] and bond torsion with subsequent restructuring of conjugated systems has been demonstrated.[24]–[27] However, the multi-step syntheses of these constructs are tedious and occasionally low yielding. Solving this, Weder, Schrettl, and coworkers have developed a readily obtainable folded perylene diimide loop,[28] which shows strain-correlated mechanochromism in commodity polymers.[29] This has inspired us to investigate whether we could reduce the synthetic complexity of mechanochromic force sensors even further while simultaneously opening up new application fields.
Therefore, we here report the development of a series of pyrene-based macrocrosslinkers (PyMCs) with supramolecular mechanochromism, which we incorporate into hydrogels formed with star-shaped poly(ethylene glycol) (sPEG; [Figure 1]). We achieve this by copolymerization of tetraethylene glycol methyl ether methacrylamide (TEGMEMAAm) and pyrene methacrylamide (PyMAAm) yielding water-soluble PyMC chains. We deliberately choose to incorporate PyMC into sPEG hydrogels due to their regular network structure leading to outstanding mechanical properties. Unlike randomly crosslinked networks, sPEG hydrogels evenly distribute applied mechanical loads on all bonds and dissipate mechanical energy by controlled uncoiling[30] of the network segments.[31]–[35] This renders any detection of force-induced events using optical force probes[36] based on covalent bond scission difficult and hence serves as an ideal proof-of-concept application for our mechanochromic macrocrosslinkers. We show that PyMC endows the sPEG hydrogels with reversible mechanochromic behavior in the elastic deformation regime. While pyrene has been investigated as mechanochromic unit in polymers before,[37]–[39] the observed emission changes have been fairly small and the conception of distinct macrocrosslinkers and their application in sPEG hydrogels is unknown.
#
Results and Discussion
Synthesis and Optical Properties of Macrocrosslinkers and Hydrogels
The hydrophobic pyrene units were incorporated into water-soluble PyMC chains by reversible addition–fragmentation chain-transfer (RAFT) polymerization starting from a bifunctional chain transfer agent (CTA), the one-step synthesis of which we reported before.[40] The water-soluble polymers of several widely employed monomers, such as N-isopropylacrylamide (NIPAAm) or N-vinylcaprolactam (VCL), exhibit lower critical solution temperatures (LCSTs) at 32.0 and 33.5 °C, respectively. Phase separation occurs above the LCST.[41] Since the copolymerization with hydrophobic monomers decreases the LCST (occasionally even below ambient temperature),[42] the desirable incorporation of high pyrene concentrations for strong fluorescence signals would have been unattainable with most common water-soluble polymers. Therefore, we synthesized copolymers of TEGMEMAAm and PyMAAm by statistical RAFT copolymerization ([Scheme 1]). We aimed at the incorporation of ca. 70 monomer units resulting in PyMCs with a contour length shorter than the commercial 10 kDa HS-PEG-SH employed as a co-crosslinker for hydrogel production. This was to ensure that PyMC would be extended first upon mechanically loading the hydrogel. The co-crosslinker was necessary to control the overall pyrene concentration in the hydrogels. The intrinsically high water-solubility of TEGMEMAAm was exploited to maintain a high water-solubility of the PyMCs even at high pyrene fractions, which ranged from 1 to 40 mol%. In the following text, the pyrene content of the PyMCs in mol% is denoted as subscript, e.g., PyMC40 for 40 mol% pyrene. Since the LCST behavior is also concentration-dependent,[43] the macrocrosslinkers started to exhibit turbidity at high PyMC concentrations from PyMC40 upwards. Therefore, PyMC32 was identified as an ideal compromise between solubility and a strong fluorescence signal and hence subsequently used for further investigation and the synthesis of the hydrogels.
Expectedly, the ratio of the excimer emission band at 480 nm and the third vibronic monomer emission band at 396 nm (I E/I M3) increased with increasing PyMC32 concentration ([Figure 2]). In earlier work we found that this was caused by either increasing interchain excimer formation dominating over intrachain excimer formation or by increasing interchain hydrodynamic compression due to passing the overlap concentration.[40] While PyMC40 showed high excimer emission in a broad concentration regime, control PyMC01 bearing exactly one pyrene unit per chain showed no excimer emission at all (Scheme S1 and Figure S1).
Hydrogels were then synthesized using four-arm vinyl sulfone-terminated sPEG (M n = 10 kDa), co-crosslinker HS-PEG-SH (M n = 10 kDa), and PyMC32 in H2O with Et3 N ([Figure 1]).[40] The PyMC32 concentration was varied while the overall reactant composition was maintained constant by compensation with HS-PEG-SH to maintain identical mechanical properties of the hydrogels. The hydrogels were purified by swelling in a DMSO/THF mixture and subsequent replacement of the solvent with H2O. To obtain mechanoresponsive hydrogels that use the indicative I E/I M3 ratio as output signal, a suitable PyMC32 concentration within the hydrogels must be identified ([Figure 3] and Table S1). At low PyMC32 concentrations, I E/I M3 converged to a minimum and fluorescence measurements were dominated by noise due to the low pyrene content. With increasing PyMC32 concentration, I E/I M3 also increased until the fluorescence spectra were dominated by the excimer emission band and I M3 was hardly measurable. For further characterization, we hence chose PyMC32 concentrations c PyMC between 2.7 · 10−5 and 1.4 · 10−4 mol · L−1 to achieve a reasonable compromise between measurable I E/I M3 ratios and a high overall fluorescence intensity.
#
Photostability of Macrocrosslinkers and Hydrogels
Subsequently, we investigated the photostability of PyMC32 and PyMC32 -crosslinked hydrogels. Pristine pyrene is photostable and not prone to photobleaching.[44] However, others and we showed that pyrene esters undergo photoinduced solvolysis[40],[45] leading to a rapidly decreasing I E and increasing I M featuring an isostilbic point.[4] We hypothesized that pyrene amides, as in the employed PyMAAm, would not show such behavior. Emission spectra taken over the course of the irradiation of aqueous PyMC32 solutions revealed a decrease in I E ([Figure 4]a). However, this was significantly slower compared to the photoinduced solvolysis of pyrene esters and showed neither an increase in I M3 nor an isostilbic point ([Figure 4]b). O2 did not contribute to this process since similar experiments under a N2 atmosphere showed comparable trends (Figure S2). While the origin of this effect remains unclear, we speculate that it may result from the complex interactions of pyrene in hydrophilic environments. Excimer formation is usually the result of diffusion-controlled interaction of a pyrene in the ground state with a pyrene in the excited state.[46] Pyrene was shown to form preassociated excimers in aqueous environments.[44] The excitation of such preassociates may lead to a separation of the ground and excited state pyrenes, which may cause the loss of excimer emission. However, we found that this effect was very slow in hydrogels and hence negligible in the investigated timeframes for mechanical analysis ([Figure 5]).
#
Influence of the Degree of Swelling on Hydrogel Emission
In addition to the PyMC concentration, we investigated the influence of the degree of swelling (d s) on the I E/I M3 ratio, which was calculated from the masses of the dry polymer (m d) and of added H2O (m w) using [Equation 1]. Equilibrium swelling was reached when the sample mass was constant for 3 d upon immersion in excess H2O. We used a hydrogel with a PyMC32 mass concentration of ρ PyMC = 2.08 · 10−4 g · L−1 ([Figure 6]). Only little variation of I E/I M3 upon varying d s occurred in the investigated swelling regime from 1000 to 8000%. However, we found in earlier work that considerably dried hydrogels with a very low d s reached a threshold value where I E/I M3 decreased steeply to almost no excimer emission at all caused by the dissolution of preassociated pyrene within the polymer backbone.[40] This implied that it was critical to prevent the hydrogels from drying out over the course of the performed measurements. Since we observed that mechanical testing in uniaxial extension mode led to rapid drying effects, we hence performed subsequent mechanical testing in uniaxial compression mode.
#
Mechanochromic Hydrogel Response
To investigate the mechanochromic properties of the PyMC32 hydrogels, we used three different variants with ρ PyMC ranging from 0.025 to 0.129 g · L−1. Since the network segments of the hydrogels at equilibrium d s were already subject to maximum uncoiling and hence became rather brittle, we decided to investigate each of the three hydrogel samples at three distinct d s below equilibrium d s. The resulting nine investigated samples are denoted H1.1 to H3.3 and their associated ρ PyMC , c pyrene, and d s can be found in [Table 1].
No. |
ρ PyMC /g · L−1 |
c pyrene/10−5 mol · L−1 |
d s/% |
---|---|---|---|
a ρ PyMC and c pyrene were calculated with respect to the equilibrium d s. |
|||
H1.1 |
0.026 |
2.66 |
1352 |
H1.2 |
0.025 |
2.72 |
2804 |
H1.3 |
0.026 |
2.77 |
4255 |
H2.1 |
0.049 |
5.26 |
1352 |
H2.2 |
0.055 |
5.88 |
2804 |
H2.3 |
0.050 |
5.37 |
4255 |
H3.1 |
0.129 |
13.81 |
1352 |
H3.2 |
0.120 |
12.71 |
2804 |
H3.3 |
0.129 |
13.85 |
4255 |
To circumvent the drying effect observed under uniaxial extension, we placed the hydrogel samples between two glass plates and subjected these to maximum compression using a micrometer screw stopping shortly before the glass plates broke ([Figure 7]). For example, upon compression of H3.2, I E/I M3 decreased from 7.2 to 4.3 corresponding to a relative change of ca. 40%. Notably, I E/I M3 recovered almost fully after de-loading the hydrogel. Renewed compression then proved the reversibility of this effect measured up to 13 times (Figure S3). Importantly, we observed the mechanochromic changes in the elastic deformation regime highlighting the advantage of the excimer-based supramolecular force sensors over traditional bond scission-based optical force probes for application in soft but elastically very extendible materials.
The results were qualitatively similar for all investigated hydrogels ([Figure 8]) where deviations were observed mainly in the relative change of I E/I M3 upon compression ranging from 20 to 50%. Notably, these relative changes are considerably higher than those reported to the literature before.[37]–[39] We believe that the molecular origin of the mechanochromic behavior is the uncoiling and gliding of PyMC during hydrogel compression (and thereby lateral extension). We hypothesize that the preassociated intra- and intermolecular pyrene aggregates are broken and an increase in pyrene monomer emission is consequently observed.
Since H2 showed the largest relative changes, we subsequently used this hydrogel batch for further mechanical testing. H2.2 was loaded 3× with different defined weights. The engineering stress σ was calculated from the ratio of the force F exerted by the weight and the initial surface area of the hydrogel A 0. It became clear that I E/I M3 decreased with increasing σ ([Figure 9]). Although σ correlated to I E/I M3, the relation was non-linear. The largest changes were observed in the initial stages of the elastic deformation. At higher stresses, the relative change in I E/I M3 appeared to reach a limiting value. Mechanistically, this may be explained by the maximum possible displacement of the preassociated pyrenes from their equilibrium where residual excimer emission was caused by interchain pyrene interactions.
#
#
Conclusions
We have shown the straightforward synthesis of PyMC macrocrosslinkers that display supramolecular mechanochromism. PyMCs were obtained in a two-step reaction from monomers that are commercial or can likewise be prepared in a one-step reaction. From these, we prepared sPEG-based hydrogels. We fully characterized the fluorescence properties and photostability of PyMCs in solution and in hydrogels depending on concentration effects and degree of swelling. We then presented the reversible mechanochromic behavior of the sPEG hydrogels in the elastic deformation regime. Thereby, we provide a protocol for the facile synthesis of mechanochromic hydrogels and anticipate that this will incentivize easier entry into the field for non-chemical researchers.
#
Experimental Section
Materials. The bifunctional CTA was synthesized in one step according to our previously published protocol.[40] Et3 N (99.5%, dry, 121-44-8), 4-(dimethylamino)pyridine (99%, DMAP, 1122-58-3), 1,6-diaminohexane (98%, 124-09-4), methacryloyl chloride (97%, 920-46-7), and AIBN (98%, 78-67-1) were obtained from Merck. AIBN was recrystallized from hexane before use. CH2Cl2 (99.9%, dry, 75-09-2), THF (99.9%, 109-99-9), MeOH (99.9%, 67-56-1), EtOAc (99.8%, 141-78-6), and DMF (99.8%, 68-12-2) were obtained from Acros Organics. 2,5,8,11-Tetraoxatridecan-13-amine (98%, 85 030-56-4), pyren-1-ylmethanaminium chloride (97%, 93 324-65-3), and TCEP (99%) were bought from abcr. Dialysis membranes were bought from Spectrum Labs (MWCO: 10 kDa). SH-PEG-SH (M n = 10 kDa, X n = 222, 99%) and 4-arm vinylsulfone-terminated sPEG (M n = 10 kDa, 99%) were obtained from Creative PEGworks.
Methods. NMR spectra were recorded at room temperature in CDCl3 on a 400 MHz Bruker Avance 400 (13C: 101 MHz). Chemical shifts were reported in δ units using residual protonated solvent signals as the internal standard. Mass spectrometry was conducted with HRMS Bruker microOTOF-Q II employing electron spray ionization ESI+. MeOH : H2O : HCOOH = 80 : 20 : 0.1 was used as a solvent. Molar masses (M n and M w) and dispersities (Đ M) were determined by gel permeation chromatography (GPC). Samples were filtered through a CHROMAFIL PTFE membrane with 0.45 µm pore size. GPC with THF (≥ 99.7%, unstabilized, HiPerSolv CHROMANORM® HPLC grade, VWR) as the eluent: HPLC pump (1260 Infinity II, Agilent), a refractive index (RI) (1290 Infinity II, Agilent), a UV- (UV-2075plus, Jasco) and a multi-angle light scattering detector (SLD 7100, Polymer Standards Service). The samples contained 250 mg · mL−1 3,5-di-tert-4-butylhydroxytoluene (BHT, ≥ 99%, Fluka) as the internal standard. 1 pre-column (8 × 50 mm) and 4 SDplus gel columns (8 × 300 mm, MZ Analysentechnik) were applied at a flow rate of 1.0 mL · min−1 at 20 °C. The diameter of the gel particles measured 5 µm, and the nominal pore widths were 50, 102, 103, and 104 Å. GPC with DMF (≥ 99.9%, HiPerSolv CHROMANORM® HPLC grade, VWR) as the eluent: HPLC pump (1260 Infinity, Agilent), a dual RI/Visco (ETA-2020, WGE), and a UV-detector (VWD, 1290 Infinity II, Agilent). The eluent contained 1 g · L−1 LiBr (≥ 99%, Sigma-Aldrich). The samples contained 2 µL · mL−1 toluene (≥ 99%, Sigma-Aldrich) as the internal standard. One pre-column (8 × 50 mm) and three GRAM gel columns (8 × 300 mm, Polymer Standards Service) were applied at a flow rate of 1.0 mL · min−1 at 60 °C. The diameter of the gel particles measured 10 µm, the nominal pore widths were 30, 102, and 103 Å. Calibration was performed using narrowly distributed poly(methyl methacrylate) standards (Polymer Standards Service). Results were evaluated using the PSS WinGPC UniChrom software (version 8.3.2).
Procedures
Optical experiments. UV-vis absorption spectroscopy was performed on a Thermo Scientific Evolution 300 and fluorescence spectroscopy on a Horiba Fluoromax-4P at room temperature in H2O (VWR, HPLC grade) and THF (VWR, Reag. Ph Eur). Excitation and emission spectra of the hydrogels were recorded with a compact spectrometer (CCS200, Thorlabs). A fiber-coupled LED (M340F3, Thorlabs) was used as a light source. The emission was detected simultaneously with the excitation with a fiber Y-bundle reflection probe (RP24, Thorlabs), which also transmitted the excitation light. The spectra were analyzed with the Thorlabs OSA software (version 2.90).
Compression experiments. A rectangular hydrogel sample (ca. 5 × 5 mm) was cut out by a scalpel. This was placed on the surface of a microscopy-grade glass slide and the surface area was determined with a caliper. Afterwards, the sample was covered with a second glass slide and placed on a pedestal. Force was applied by placing defined metal weights on top of the cover slide. The deformed hydrogel increased in surface but did not exit the glass slide edges. The compressed surface area was determined again with a caliper through the bottom glass slide.
Synthesis of TEGMEMAAm. 2,5,8,11-Tetraoxatridecan-13-amine (0.91 g, 4.40 mmol) was dissolved in dry THF (20 mL) with DMAP (0.108 g, 0.88 mmol). The flask was flushed with Ar for 7 min and then dry Et3 N (0.39 mL, 5.29 mmol) was added. Then, methacryloyl chloride (0.33 mL, 4.85 mmol) was added dropwise at 0 °C under Ar. The reaction was stirred and slowly warmed to r. t. overnight. The reaction was quenched with aq. Na2CO3 solution and then extracted with CH2Cl2. The organic layer was washed with 0.1 M aq. HCl, brine, and then dried over MgSO4. The solvent was evaporated in vacuo and the product was purified by silica column chromatography with EtOAc and MeOH (95 : 5, R f = 0.35). A yellow oil was obtained (87%). 1H NMR (CDCl3): δ (ppm): 6.50 (s, 1 H, NH), 5.70 (s, 1 H, vinyl), 5.30 (s, 1 H, vinyl), 3.60 (m, 18 H, -O-CH2-CH2-O-), 3.36 (s, 3 H, O-CH3), 1.96 (s, 3 H, CH3). See Figure S7. 13C NMR (CDCl3): 120.0, 72.4, 71 – 70, 59.5, 39.9, 19.1. See Figure S8. HRMS (ESI+): m/z calcd. for C13H25NNaO5 +: 298.1625; found: 298.1495. See Figure S9.
Synthesis of PyMAAm. Pyren-1-ylmethanaminium chloride (2.46 g, 10.20 mmol) was added to a reaction flask, dried in vacuo, and then suspended in dry THF (100 mL). By adding DMAP (0.25 g, 2.04 mmol) and Et3 N (3.11 mL, 22.40 mmol), the suspension slowly dissolved. The reaction mixture was stirred for 30 min. Then, methacryloyl chloride was added dropwise at 0 °C and the reaction was stirred at r. t. overnight. The reaction was then diluted with EtOAc and extracted 3× with 0.1 M aq. HCl and 3× with brine. The organic layer was dried over MgSO4, collected, and the solvent was evaporated. The product was purified by silica column chromatography with CH2Cl2 and EtOH (97 : 3, R f = 0.5) yielding a white-yellow solid (91%). 1H NMR (CDCl3): δ (ppm): 8.05 (m, 9 H, aromatic), 6.12 (s, 1 H, NH), 5.69 (s, 1 H, vinyl), 5.32 (s, 1 H, vinyl), 5.21 (m, 2 H, -CH2-N-), 1.98 (s, 3 H, -CH3). See Figure S10. 13C NMR (CDCl3): 140.3, 131.8 – 129.6, 125.5, 125.2, 120.2, 42.7, 19.2. See Figure S11. HRMS (ESI+): m/z calcd. for C21H18 NO+: 300.1383; found: 300.1248. See Figure S12.
General procedure for PyMC synthesis. The bifunctional CTA (1 equiv.) was used in statistical copolymerizations of PyMAAm (2 · o equiv.) and TEGMEMAAm (2 · n = 70 – 2 · o equiv.) in dry DMSO (66 wt%), cf. [Scheme 1]. To this, AIBN (0.4 equiv.) was added, and the solution was kept at 67 °C for 18 h achieving conversions > 90% as determined by 1H NMR. The obtained polymers were dialyzed against THF and then against H2O. Yellow polymers were obtained with typical yields of ~90%. The polymers were analyzed by 1H NMR and GPC (Figures S17 – S19). The feed fraction of PyMAAm during polymerization was slightly higher than the incorporated fraction that was found in the polymer. Afterwards, the terminal trithiocarbonates were aminolyzed by the addition of n-butylamine (30 equiv.) under Schlenk conditions in THF (0.012 mol · L−1) in the presence of TCEP (ca. 1 mg). Hereafter, the polymer was dialyzed against THF and then H2O, dried in vacuo, and colorless PyMCs were received. Đ M was typically ~1.3 (Figure S18).
General procedure for hydrogel preparation. Polymerization was performed by step-growth polymerization of PyMC macrocrosslinkers (z equiv.) alongside HS-PEG-SH (2-z equiv., 10 kDa) and 4-armed sPEG terminally functionalized with 4× vinyl sulfone (1 equiv.) via a thiol-ene reaction at pH = 8 – 10. Exemplarily, sPEG (1.3 µmol, 6.60 mg), HS-PEG-SH (2.66 µmol, 26.66 mg), and PyMC (0.068 mg) were dissolved in H2O (200 µL) and cast into a PTFE-coated metal mold. After the addition of Et3 N (30 µL), the mold was covered and left to react overnight. The hydrogels were immersed first in DMSO/THF then in H2O to remove residual reactants yielding transparent hydrogels with visible blue or green fluorescence based on the identity and fraction of the incorporated PyMC.
#
Funding Information
D. R. and R. G. are grateful for support by a Freigeist-Fellowship of the Volkswagen Foundation (92 888). Parts of the analytical investigations were performed at the Center for Chemical Polymer Technology CPT, which was supported by the European Commission and the federal state of North Rhine-Westphalia (300 088 302).
#
#
#
Conflict of Interest
The authors declare no conflict of interest.
Primary Data
Primary Data for this article are available online at https://zenodo.org/record/6984827.
-
References
- 1 Förster T, Kasper KZ. Elektrochem. Ber. Bunsenges. Phys. Chem. 1955; 59: 976
- 2 Birks JB, Dyson DJ, Munro IH, Flowers BH. Proc. R. Soc. London, Ser. A 1963; 275: 575
- 3 de Halleux V, Mamdouh W, De Feyter S, De Schryver F, Levin J, Geerts YH. J. Photochem. Photobiol., A 2006; 178: 251
- 4 Förster T. Angew. Chem. Int. Ed. Engl. 1969; 8: 333
- 5 Figueira-Duarte TM, Müllen K. Chem. Rev. 2011; 111: 7260
- 6 Pietsch C, Vollrath A, Hoogenboom R, Schubert US. Sensors 2010; 10: 7979
- 7 Dembska A, Juskowiak B. Spectrochim. Acta, Part A 2015; 150: 928
- 8 Claucherty S, Sakaue H. Sens. Actuator, A 2021; 317: 112359
- 9 Kovalev IS, Taniya OS, Slovesnova NV, Kim GA, Santra S, Zyryanov GV, Kopchuk DS, Majee A, Charushin VN, Chupakhin ON. Chem. Asian J. 2016; 11: 775
- 10 Bains G, Patel AB, Narayanaswami V. Molecules 2011; 16: 7909
- 11 Somerharju PChem. Phys. Lipids 2002; 116: 57
- 12 Krasheninina OA, Novopashina DS, Apartsin EK, Venyaminova AG. Molecules 2017; 22: 2108
- 13 Sagara Y, Yamane S, Mitani M, Weder C, Kato T. Adv. Mater. 2016; 28: 1073
- 14 Calvino C, Neumann L, Weder C, Schrettl S. J. Polym. Sci., Part A: Polym. Chem. 2017; 55: 640
- 15 Traeger H, Kiebala DJ, Weder C, Schrettl S. Macromol. Rapid Commun. 2021; 42: 2000573
- 16 Löwe C, Weder C. Adv. Mater. 2002; 14: 1625
- 17 OʼNeill RT, Boulatov R. Nat. Rev. Chem. 2021; 5: 148
- 18 Chen Y, Mellot G, Luijk Dvan, Creton C, Sijbesma RP. Chem. Soc. Rev. 2021; 50: 4100
- 19 Sagara Y, Karman M, Verde-Sesto E, Matsuo K, Kim Y, Tamaoki N, Weder C. J. Am. Chem. Soc. 2018; 140: 1584
- 20 Muramatsu T, Sagara Y, Traeger H, Tamaoki N, Weder C. ACS Appl. Mater. Interfaces 2019; 11: 24571
- 21 Sagara Y, Karman M, Seki A, Pannipara M, Tamaoki N, Weder C. ACS Cent. Sci. 2019; 5: 874
- 22 Muramatsu T, Okado Y, Traeger H, Schrettl S, Tamaoki N, Weder C, Sagara Y. J. Am. Chem. Soc. 2021; 143: 9884
- 23 Sagara Y, Traeger H, Li J, Okado Y, Schrettl S, Tamaoki N, Weder C. J. Am. Chem. Soc. 2021; 143: 5519
- 24 van de Laar T, Schuurman H, van der Scheer P, Maarten van Doorn J, van der Gucht J, Sprakel J. Chem 2018; 4: 269
- 25 Raisch M, Maftuhin W, Walter M, Sommer M. Nat. Commun. 2021; 12: 4243
- 26 Raisch M, Reiter G, Sommer M. ACS Macro Lett. 2022; 11: 760
- 27 Hu H, Cheng X, Ma Z, Sijbesma RP, Ma Z. J. Am. Chem. Soc. 2022; 144: 9971
- 28 Traeger H, Sagara Y, Kiebala DJ, Schrettl S, Weder C. Angew. Chem. Int. Ed. 2021; 60: 16191
- 29 Traeger H, Sagara Y, Berrocal JA, Schrettl S, Weder C. Polym. Chem. 2022; 13: 2860
- 30 Liese S, Gensler M, Krysiak S, Schwarzl R, Achazi A, Paulus B, Hugel T, Rabe JP, Netz RR. ACS Nano 2017; 11: 702
- 31 Lutolf MP, Hubbell JA. Biomacromolecules 2003; 4: 713
- 32 Rehmann MS, Skeens KM, Kharkar PM, Ford EM, Maverakis E, Lee KH, Kloxin AM. Biomacromolecules 2017; 18: 3131
- 33 Wang J, Zhang F, Tsang WP, Wan C, Wu C. Biomaterials 2017; 120: 11
- 34 Licht C, Rose JC, Anarkoli AO, Blondel D, Roccio M, Haraszti T, Gehlen DB, Hubbell JA, Lutolf MP, De Laporte L. Biomacromolecules 2019; 20: 4075
- 35 Grad EM, Tunn I, Voerman D, de Léon AS, Hammink R, Blank KG. Front. Chem. 2020; 8: 536
- 36 He S, Stratigaki M, Centeno SP, Dreuw A, Göstl R. Chem. Eur. J. 2021; 27: 15889
- 37 Rossi NAA, Duplock EJ, Meegan J, Roberts DRT, Murphy JJ, Patel M, Holder SJ. J. Mater. Chem. 2009; 19: 7674
- 38 Roberts DRT, Patel M, Murphy JJ, Holder SJ. Sens. Actuators, B 2012; 162: 43
- 39 Cellini F, Block L, Li J, Khapli S, Peterson SD, Porfiri M. Sens. Actuators, B 2016; 234: 510
- 40 Rasch D, Göstl R. ACS Polym. Au 2021; 1: 59
- 41 Roy D, Brooks WLA, Sumerlin BS. Chem. Soc. Rev. 2013; 42: 7214
- 42 Schild HG. Prog. Polym. Sci. 1992; 17: 163
- 43 Chua GBH, Roth PJ, Duong HTT, Davis TP, Lowe AB. Macromolecules 2012; 45: 1362
- 44 Winnik FM. Chem. Rev. 1993; 93: 587
- 45 Iwamura M, Ishikawa T, Koyama Y, Sakuma K, Iwamura H. Tetrahedron Lett. 1987; 28: 679
- 46 Birks JB. Nature 1967; 214: 1187
Correspondence
Publication History
Received: 12 August 2022
Accepted after revision: 16 September 2022
Article published online:
26 October 2022
© 2022. The authors. This is an open access article published by Thieme under the terms of the Creative Commons Attribution License, permitting unrestricted use, distribution, and reproduction so long as the original work is properly cited. (https://creativecommons.org/licenses/by/4.0/).
Georg Thieme Verlag KG
Rüdigerstraße 14, 70469 Stuttgart, Germany
-
References
- 1 Förster T, Kasper KZ. Elektrochem. Ber. Bunsenges. Phys. Chem. 1955; 59: 976
- 2 Birks JB, Dyson DJ, Munro IH, Flowers BH. Proc. R. Soc. London, Ser. A 1963; 275: 575
- 3 de Halleux V, Mamdouh W, De Feyter S, De Schryver F, Levin J, Geerts YH. J. Photochem. Photobiol., A 2006; 178: 251
- 4 Förster T. Angew. Chem. Int. Ed. Engl. 1969; 8: 333
- 5 Figueira-Duarte TM, Müllen K. Chem. Rev. 2011; 111: 7260
- 6 Pietsch C, Vollrath A, Hoogenboom R, Schubert US. Sensors 2010; 10: 7979
- 7 Dembska A, Juskowiak B. Spectrochim. Acta, Part A 2015; 150: 928
- 8 Claucherty S, Sakaue H. Sens. Actuator, A 2021; 317: 112359
- 9 Kovalev IS, Taniya OS, Slovesnova NV, Kim GA, Santra S, Zyryanov GV, Kopchuk DS, Majee A, Charushin VN, Chupakhin ON. Chem. Asian J. 2016; 11: 775
- 10 Bains G, Patel AB, Narayanaswami V. Molecules 2011; 16: 7909
- 11 Somerharju PChem. Phys. Lipids 2002; 116: 57
- 12 Krasheninina OA, Novopashina DS, Apartsin EK, Venyaminova AG. Molecules 2017; 22: 2108
- 13 Sagara Y, Yamane S, Mitani M, Weder C, Kato T. Adv. Mater. 2016; 28: 1073
- 14 Calvino C, Neumann L, Weder C, Schrettl S. J. Polym. Sci., Part A: Polym. Chem. 2017; 55: 640
- 15 Traeger H, Kiebala DJ, Weder C, Schrettl S. Macromol. Rapid Commun. 2021; 42: 2000573
- 16 Löwe C, Weder C. Adv. Mater. 2002; 14: 1625
- 17 OʼNeill RT, Boulatov R. Nat. Rev. Chem. 2021; 5: 148
- 18 Chen Y, Mellot G, Luijk Dvan, Creton C, Sijbesma RP. Chem. Soc. Rev. 2021; 50: 4100
- 19 Sagara Y, Karman M, Verde-Sesto E, Matsuo K, Kim Y, Tamaoki N, Weder C. J. Am. Chem. Soc. 2018; 140: 1584
- 20 Muramatsu T, Sagara Y, Traeger H, Tamaoki N, Weder C. ACS Appl. Mater. Interfaces 2019; 11: 24571
- 21 Sagara Y, Karman M, Seki A, Pannipara M, Tamaoki N, Weder C. ACS Cent. Sci. 2019; 5: 874
- 22 Muramatsu T, Okado Y, Traeger H, Schrettl S, Tamaoki N, Weder C, Sagara Y. J. Am. Chem. Soc. 2021; 143: 9884
- 23 Sagara Y, Traeger H, Li J, Okado Y, Schrettl S, Tamaoki N, Weder C. J. Am. Chem. Soc. 2021; 143: 5519
- 24 van de Laar T, Schuurman H, van der Scheer P, Maarten van Doorn J, van der Gucht J, Sprakel J. Chem 2018; 4: 269
- 25 Raisch M, Maftuhin W, Walter M, Sommer M. Nat. Commun. 2021; 12: 4243
- 26 Raisch M, Reiter G, Sommer M. ACS Macro Lett. 2022; 11: 760
- 27 Hu H, Cheng X, Ma Z, Sijbesma RP, Ma Z. J. Am. Chem. Soc. 2022; 144: 9971
- 28 Traeger H, Sagara Y, Kiebala DJ, Schrettl S, Weder C. Angew. Chem. Int. Ed. 2021; 60: 16191
- 29 Traeger H, Sagara Y, Berrocal JA, Schrettl S, Weder C. Polym. Chem. 2022; 13: 2860
- 30 Liese S, Gensler M, Krysiak S, Schwarzl R, Achazi A, Paulus B, Hugel T, Rabe JP, Netz RR. ACS Nano 2017; 11: 702
- 31 Lutolf MP, Hubbell JA. Biomacromolecules 2003; 4: 713
- 32 Rehmann MS, Skeens KM, Kharkar PM, Ford EM, Maverakis E, Lee KH, Kloxin AM. Biomacromolecules 2017; 18: 3131
- 33 Wang J, Zhang F, Tsang WP, Wan C, Wu C. Biomaterials 2017; 120: 11
- 34 Licht C, Rose JC, Anarkoli AO, Blondel D, Roccio M, Haraszti T, Gehlen DB, Hubbell JA, Lutolf MP, De Laporte L. Biomacromolecules 2019; 20: 4075
- 35 Grad EM, Tunn I, Voerman D, de Léon AS, Hammink R, Blank KG. Front. Chem. 2020; 8: 536
- 36 He S, Stratigaki M, Centeno SP, Dreuw A, Göstl R. Chem. Eur. J. 2021; 27: 15889
- 37 Rossi NAA, Duplock EJ, Meegan J, Roberts DRT, Murphy JJ, Patel M, Holder SJ. J. Mater. Chem. 2009; 19: 7674
- 38 Roberts DRT, Patel M, Murphy JJ, Holder SJ. Sens. Actuators, B 2012; 162: 43
- 39 Cellini F, Block L, Li J, Khapli S, Peterson SD, Porfiri M. Sens. Actuators, B 2016; 234: 510
- 40 Rasch D, Göstl R. ACS Polym. Au 2021; 1: 59
- 41 Roy D, Brooks WLA, Sumerlin BS. Chem. Soc. Rev. 2013; 42: 7214
- 42 Schild HG. Prog. Polym. Sci. 1992; 17: 163
- 43 Chua GBH, Roth PJ, Duong HTT, Davis TP, Lowe AB. Macromolecules 2012; 45: 1362
- 44 Winnik FM. Chem. Rev. 1993; 93: 587
- 45 Iwamura M, Ishikawa T, Koyama Y, Sakuma K, Iwamura H. Tetrahedron Lett. 1987; 28: 679
- 46 Birks JB. Nature 1967; 214: 1187